| NO. | CHARACTERISTICS | REQUREMENT (AS PER ISO 13006 BIa / EN 176 BI a) | ISO / EN TESTING METHOD |
|---|---|---|---|
| A | DIMENSION & SURFACE QUALITY | ||
| 1 | Deviation in Length & width | Max. +/- 0.5% | EN-98;IS:13630 (Part 1) |
| 2 | Deviation in thickness | Max. +/- 5% | EN-98;IS:13630 (Part 1) |
| 3 | Surface flatness (Warpage) | Max. +/- 0.5% | EN-98;IS:13630 (Part 1) |
| 4 | Rectangularity (Squareness) | Max. +/- 0.5% | EN-98;IS:13630 (Part 1) | B | PHYSICAL PROPERTIES |
| 1 | Water Absorption | >/= 10% | EN-99;IS:13630 (Part 2) |
| 2 | Scratch Hardness of Surface (Mohs) | Min. 3 | EN-101;IS:13630 (Part 13) |
| 3 | Resistance to Surface Abrasion (of tiles intended for use on floors) | Abration class shall be specified by the manufacturer | EN-154;IS:13630 (Part 11) |
| 4 | Crazing Resistance | Required | EN-105;IS:13630 (Part 9) |
| 5 | Modulus of Rupture | Min.153 Kg/cm2 | EN-100;IS:13630 (Part 6) | C | CHEMICAL / THERMAL PROPERTIES |
| 1 | STAINING RESISTANCE | MIN CLASS 2 | EN-122;IS:13630 (Part 8) |
| 2 | HOUSEHOLD CHEMICALS | MIN CLASS B | EN-122;IS:13630 (Part 8) |
| 3 | THERMAL SHOCK | RESISTANT TO 10 CYCLES | EN-104;IS:13630 (Part 5) |
| 4 | THERMAL EXPANSION | MAX-9E-06 | EN-104;IS:13630 (Part 5) |
Οι τεχνικές προδιαγραφές για τα ψηφιακά πλακάκια τοίχων με βάση το ISO 13006 BIA / EN 176 BI A Πρότυπα. Χωρίζεται σε τρία κύρια τμήματα: Διάσταση και ποιότητα επιφάνειας, φυσικές ιδιότητες και χημικές / θερμικές ιδιότητες.
Η ποιότητα των διαστάσεων και της επιφάνειας εξασφαλίζει ότι τα πλακάκια συμμορφώνονται με συγκεκριμένα πρότυπα όσον αφορά το μέγεθος, το σχήμα και την ομοιομορφία της επιφάνειας. Οι αποδεκτές αποκλίσεις σε μήκος, πλάτος και πάχος ρυθμίζονται αυστηρά για να διατηρήσουν τη συνοχή στα πλακάκια. Σύμφωνα με τα πρότυπα, τα κεραμίδια μπορούν να έχουν μέγιστη απόκλιση +/- 0,5% σε μήκος και πλάτος και +/- 5% σε πάχος. Επιπλέον, τα κεραμίδια πρέπει να έχουν ελάχιστη περιποίηση (max +/- 0,5%) για να εξασφαλίσουν επιπεδότητα και θα πρέπει να είναι τετράγωνο με αποδεκτή απόκλιση +/- 0,5% στην ορθογώνια. Αυτές οι μετρήσεις είναι ζωτικής σημασίας για τα πλακάκια να ταιριάζουν σωστά κατά τη διάρκεια της εγκατάστασης και να διατηρήσουν μια ομοιόμορφη οπτική επιφάνεια.
Οι φυσικές ιδιότητες ορίζουν την απόδοση του πλακιδίου σε πραγματικές συνθήκες, ειδικά όταν υπόκεινται σε φυσικό στρες. Πρώτον, η απορρόφηση του νερού πρέπει να είναι ≥10%, πράγμα που υποδεικνύει πόσο πορώδες είναι το πλακίδιο και η καταλληλότητά του για διαφορετικά περιβάλλοντα (η υψηλότερη απορρόφηση νερού βρίσκεται γενικά στα πλακάκια τοίχων). Η σκληρότητα της γρατσουνιάς της επιφάνειας, που μετράται στην κλίμακα MOHS, πρέπει να είναι τουλάχιστον 3, γεγονός που δίνει μια ιδέα για το πόσο ανθεκτικό είναι το πλακάκι να γρατζουνίζει από κοινά αντικείμενα. Τα κεραμίδια που προορίζονται για χρήση δαπέδου πρέπει να πληρούν τις απαιτήσεις αντίστασης τριβής, με τον κατασκευαστή να καθορίζει την κλάση τριβής. Τα κεραμίδια πρέπει επίσης να είναι ανθεκτικά στο τρελό (λεπτή ρωγμή) υπό κανονικές συνθήκες. Τέλος, το μέτρο ρήξης (η ικανότητα του πλακιδίου να αντέχει στο σπάσιμο) πρέπει να είναι τουλάχιστον 153 kg/cm2, εξασφαλίζοντας ότι τα κεραμίδια είναι αρκετά ισχυρά ώστε να χειρίζονται τις εξωτερικές δυνάμεις.
Οι χημικές / θερμικές ιδιότητες υπογραμμίζουν την αντίσταση των πλακιδίων σε λεκέδες, χημικές ουσίες και θερμικές αλλαγές. Η αντίσταση χρώσης, με ελάχιστη απαίτηση της κατηγορίας 2, εξασφαλίζει ότι τα κεραμίδια μπορούν να αντέξουν την έκθεση σε κοινές ουσίες χρώσης χωρίς μόνιμο αποχρωματισμό. Τα κεραμίδια πρέπει επίσης να αντισταθούν σε ζημιές από τις οικιακές χημικές ουσίες, ταξινομημένες σε ελάχιστη κατηγορία Β, καθιστώντας τα κατάλληλα για κουζίνες και μπάνια όπου η έκθεση σε καθαριστικούς παράγοντες είναι κοινή. Για θερμική ανθεκτικότητα, τα κεραμίδια πρέπει να είναι σε θέση να αντισταθούν σε τουλάχιστον 10 κύκλους θερμικού σοκ, εξασφαλίζοντας ότι μπορούν να χειριστούν ξαφνικές αλλαγές στη θερμοκρασία χωρίς ρωγμές. Επιπλέον, ο συντελεστής θερμικής διαστολής δεν πρέπει να υπερβαίνει το 9Ε-06, που σημαίνει ότι τα κεραμίδια θα επεκταθούν μόνο ελάχιστα όταν εκτίθενται σε θερμότητα, διατηρώντας τη δομική ακεραιότητά τους με την πάροδο του χρόνου.
| NO. | CHARACTERISTICS | REQUREMENT (AS PER ISO 13006 BIIa / EN 176 BII a) | ISO / EN TESTING METHOD | A | DIMENSION & SURFACE QUALITY |
|---|---|---|---|
| 1 | Deviation in Length & Width | ||
| a.The deviation in percent of the average size of each tile (2 or 4 sides) from the work size (w) | Max.± 0.6 | ISO-10545-2 IS:13630-1 | |
| b. The deviation in percent of the average size of each tile (2 or 4 sides) from the average size of the 10 test specimen (20 or 40 sides) | Max.± 0.5 | ISO-10545-2 IS:13630-1 | |
| 2 | Deviation in Thickness | Max.± 5.0% | ISO-10545-2 IS:13630-1 |
| 3 | Deviation in Straightness of sides | Max.±0.5% | ISO-10545-2 IS:13630-1 |
| 4 | Deviation in Rectangulanty | Max.±0.6% | ISO-10545-2 IS:13630-1 |
| 5 | Surface Flatness | ||
| a.Centre curvature (max.) | Max.± 0.5% | ISO-10545-2 IS:13630-1 | |
| b.Edge curvature (max.) | Max.± 0.5% | ISO-10545-2 IS:13630-1 | |
| c.Corner warpage (max.) | Max.± 0.5% | ISO-10545-2 IS:13630-1 | B | PHYSICAL PROPERTIES |
| 1 | Water Absorption | Avg.3 < E < 6% Individual max. 6.5% | ISO-10545-3 IS:13630-2 |
| 2 | Scratch Hardness (Moh's scale) | Not Required | IS:13630-13 |
| 3 | Abrasion Resistance | Tested as per PEI methodology | ISO-10545-7 IS:13630-11 |
| 4 | Crazing Resistance | Required | ISO-10545-11 IS:13630-9 |
| 5 | Modulus of Rupture in N/mm² | Avg. 22, Individual min 20 | ISO-10545-4 IS:13630-6 | C | CHEMICAL / THERMAL PROPERTIES |
| 1 | Chemical Resistance | Required,if agreed | ISO-10545-13 IS:13630-8 |
| 2 | Resistance to household chemicals | Class AA, min. | ISO-10545-13 IS:13630-8 |
| 3 | Resistance to staining | Class 1, min. | ISO-10545-14 IS:13630-8 |
| 4 | Thermal Shock | Required,if agreed | ISO-10545-9 IS:13630-5 |
Η διάσταση και η ποιότητα της επιφάνειας περιγράφουν τις επιτρεπόμενες διακυμάνσεις στις διαστάσεις και την ποιότητα της επιφάνειας των κεραμικών πλακιδίων δαπέδου. Ορίζει τις μέγιστες επιτρεπόμενες αποκλίσεις σε μήκος, πλάτος και πάχος για να εξασφαλιστεί η ομοιομορφία και η ευκολία εγκατάστασης. Η απόκλιση του μήκους και του πλάτους χωρίζεται σε δύο μέρη: ένα που συγκρίνει το μέγεθος του πλακιδίου με το μέγεθος της εργασίας (μέγιστη απόκλιση ± 0,6%) και ένα άλλο που συγκρίνει το μέγεθος του πλακιδίου με το μέσο μέγεθος των δειγμάτων δοκιμής (μέγιστη απόκλιση ± 0,5 %). Η μέγιστη απόκλιση στο πάχος είναι ± 5%, εξασφαλίζοντας ότι τα πλακάκια είναι συνεπή στο πάχος τους. Η ευθεία των πλευρών και η ορθογώνια περιορίζονται σε μέγιστη απόκλιση ± 0,5% και ± 0,6% αντίστοιχα. Επιπλέον, η επιφάνεια της επιφάνειας μετράται με καμπυλότητα στο κέντρο και την ακμή, καθώς και τη γωνιά, το καθένα περιορίζεται σε ± 0,5% για να εξασφαλίσει μια ομαλή, ακόμη και επιφάνεια.
Οι φυσικές ιδιότητες περιγράφουν τα φυσικά χαρακτηριστικά των πλακιδίων, εστιάζοντας στην απορρόφηση νερού, τη σκληρότητα και τη δύναμη. Η απορρόφηση νερού των κεραμικών πλακιδίων δαπέδου πρέπει να κυμαίνεται μεταξύ 3%και 6%, με ατομικό μέγιστο 6,5%, καθιστώντας τα κατάλληλα για εσωτερικά δάπεδα όπου είναι απαραίτητη η αντίσταση στο νερό. Η σκληρότητα της γρατσουνιάς, που μετράται στην κλίμακα MOHS, δεν απαιτείται για κεραμικά πλακάκια δαπέδου. Η αντίσταση στην τριβή δοκιμάζεται χρησιμοποιώντας τη μέθοδο PEI, η οποία εξασφαλίζει ότι τα κεραμίδια μπορούν να αντέξουν την κυκλοφορία των ποδιών. Η ανθεκτικότητα στην τρελή είναι υποχρεωτική, εξασφαλίζοντας ότι τα κεραμίδια δεν θα αναπτύξουν καλές ρωγμές με την πάροδο του χρόνου. Το μέτρο ρήξης, το οποίο μετρά τη δύναμη των πλακιδίων, θα πρέπει να έχει μέση τιμή 22 n/mm², με ελάχιστη ατομική τιμή 20 n/mm², υποδεικνύοντας ότι μπορούν να χειριστούν σημαντική πίεση πριν από το σπάσιμο.
Οι χημικές / θερμικές ιδιότητες αξιολογούν την αντίσταση των πλακιδίων στις χημικές ουσίες, τη χρώση και το θερμικό σοκ. Τα κεραμίδια πρέπει να είναι χημικά ανθεκτικά, ειδικά εάν συμφωνηθεί αυτή η απαίτηση με τον κατασκευαστή. Πρέπει επίσης να έχουν τουλάχιστον αντίσταση κατηγορίας ΑΑ στις οικιακές χημικές ουσίες, που σημαίνει ότι μπορούν να αντέξουν την έκθεση σε κοινούς παράγοντες καθαρισμού χωρίς υποβάθμιση. Η ελάχιστη απαιτούμενη αντίσταση στη χρώση είναι η κλάση 1, εξασφαλίζοντας ότι τα πλακάκια παραμένουν καθαρά και μη χρωματισμένα σε τακτική χρήση. Απαιτείται θερμική αντοχή σε κλονισμό εάν καθορίζεται, εξασφαλίζοντας ότι τα κεραμίδια μπορούν να αντέξουν ξαφνικές αλλαγές θερμοκρασίας χωρίς ρωγμές, η οποία είναι απαραίτητη για τα πλακάκια που χρησιμοποιούνται σε περιβάλλοντα με διακυμάνσεις των θερμοκρασιών.
| NO. | CHARACTERISTICS | REQUREMENT (AS PER ISO 13006 BIa / EN 176 BIa) | ISO / EN TESTING METHOD |
|---|---|---|---|
| A | DIMENSION & SURFACE QUALITY | ||
| 1 | Deviation in length | ± 0.6% | ISO-10545-2 |
| 2 | Deviation in thickness | ± 5.0% | ISO-10545-2 |
| 3 | Straightness of sides | ± 0.5% | ISO-10545-2 |
| 4 | Rectangularity | ± 0.6% | ISO-10545-2 |
| B | PHYSICAL PROPERTIES | ||
| 1 | Water absorption | <0.5% | ISO-10545-2 |
| 2 | MOH's hardness | >6 | EN101 |
| 3 | Flexural strength | >35 N/mm2 | ISO-10545-4 |
| 4 | Abrasion resistance | <175mm3 | ISO-10545-6 |
| 5 | Breaking strength | 1113N | ISO-10545-6 |
| Density (gm/cc) | >2 | ISO-10545-3 | |
| C | CHEMICAL / THERMAL PROPERTIES | ||
| 1 | Frost resistance | Frostproof | ISO-10545-12 |
| 2 | Chemical resistance | No damage | ISO-10545-13 |
| 3 | Thermal shock resistance | No damage | ISO-10545-9 |
| 4 | Colour resistance | No damage | DIN 51094 |
| 5 | Thermal expansion | < 9 x 10-6 | ISO-10545-8 |
| 6 | Stain resistance | Resistance | ISO-10545-14 |
| 7 | Moisture expansion | Nil | ISO-10545-10 |
Η διάσταση και η ποιότητα της επιφάνειας περιγράφουν τις επιτρεπόμενες διακυμάνσεις των διαστάσεων για τα πλακάκια στάθμευσης, εξασφαλίζοντας τη συνοχή και την ακρίβεια στην παραγωγή τους. Το μήκος των πλακιδίων μπορεί να αποκλίνει κατά μέγιστο ± 0,6%και το πάχος τους κατά ± 5,0%. Η ευθεία των πλευρών και η ορθογώνια περιορίζονται σε απόκλιση ± 0,5% και ± 0,6%, αντίστοιχα, η οποία βοηθά στη διατήρηση της ομοιομορφίας κατά τη διάρκεια της εγκατάστασης. Αυτές οι ανοχές είναι κρίσιμες για την κατάλληλη ευθυγράμμιση και την εφαρμογή, εξασφαλίζοντας ότι τα κεραμίδια παρέχουν μια ομαλή και σταθερή επιφάνεια κατάλληλη για περιοχές υψηλής κυκλοφορίας όπως χώρους στάθμευσης.
Οι φυσικές ιδιότητες των πλακιδίων στάθμευσης είναι ζωτικής σημασίας για την απόδοσή τους σε υπαίθρια περιβάλλοντα. Η απορρόφηση του νερού πρέπει να είναι κάτω από 0,5%, εξασφαλίζοντας ότι τα κεραμίδια είναι ιδιαίτερα ανθεκτικά στην υγρασία και κατάλληλα για υγρές ή βροχερές συνθήκες. Τα κεραμίδια πρέπει επίσης να παρουσιάσουν βαθμολογία σκληρότητας MOHS μεγαλύτερη από 6, υποδεικνύοντας ότι είναι ιδιαίτερα ανθεκτικές στο ξύσιμο. Η αντοχή στην κάμψη πρέπει να υπερβαίνει τα 35 N/mm2, πράγμα που σημαίνει ότι τα κεραμίδια μπορούν να αντέξουν τις δυνάμεις κάμψης, ενώ η αντίσταση στην τριβή πρέπει να είναι μικρότερη από 175mm3, εξασφαλίζοντας ότι μπορούν να υπομείνουν σταθερή φθορά από οχήματα και κίνηση ποδιών. Η αντοχή θραύσης πρέπει να φτάσει το 1113n, εξασφαλίζοντας ότι τα κεραμίδια είναι ανθεκτικά κάτω από βαριά φορτία. Η πυκνότητα των πλακιδίων πρέπει να είναι μεγαλύτερη από 2 g/cm3, αντανακλώντας τη σταθερή τους κατασκευή και την ικανότητα να υπομείνει το στρες.
Τα πλακάκια στάθμευσης πρέπει να είναι σε θέση να αντέχουν σε σκληρές περιβαλλοντικές συνθήκες, συμπεριλαμβανομένης της χημικής έκθεσης και των διακυμάνσεων της θερμοκρασίας. Τα κεραμίδια είναι ανθεκτικά στον παγετό, καθιστώντας τα κατάλληλα για ψυχρότερα κλίματα. Πρέπει επίσης να αντισταθούν σε ζημιές από χημικά και θερμικό σοκ, εξασφαλίζοντας τη μακροζωία ακόμη και όταν εκτίθενται σε ακραίες συνθήκες. Η αντίσταση χρώματος εξασφαλίζει ότι τα κεραμίδια διατηρούν την εμφάνισή τους με την πάροδο του χρόνου, παρά την έκθεση στο φως του ήλιου ή στη θερμότητα. Η θερμική διαστολή περιορίζεται σε λιγότερο από 9 x 10 ⁻⁶, που σημαίνει ότι τα κεραμίδια δεν θα επεκταθούν σημαντικά με τις μεταβολές της θερμοκρασίας, διατηρώντας δομική ακεραιότητα. Πρέπει επίσης να αντισταθούν στις λεκέδες και στην επέκταση της υγρασίας, εξασφαλίζοντας ότι παραμένουν καθαροί και σταθεροί σε διάφορες καιρικές συνθήκες.
| NO. | CHARACTERISTICS | REQUREMENT (AS PER ISO 13006 BIa / EN 176 BIa) | ISO / EN TESTING METHOD |
|---|---|---|---|
| A | DIMENSION & SURFACE QUALITY | ||
| 1 | Deviation in Length | ± 0.6% | ISO-10545-2 |
| 2 | Deviation in Thickness | ± 0.5% | ISO-10545-2 |
| 3 | Straightness of Sides | ± 0.5% | ISO-10545-2 |
| 4 | Rectangularity | ± 0.6% | ISO-10545-2 |
| 5 | Surface Flatness | ± 0.5% | ISO-10545-2 |
| 6 | Glosiness | - | GLOSSMETER |
| B | STRUCTURAL PROPERTIES | ||
| 1 | Water absorption * | < 0.5% | ISO-10545-3 |
| 2 | Density (g/cc) | > 2 | DIN 51082 |
| C | MASSIVE MECHANICAL PROPERTIES | ||
| 1 | Flexural Strength * | > 27 N/mm ² | ISO-10545-4 |
| 2 | Breaking Strength * | 1113 N | ISO-10545-4 |
| D | SURFACE MECHANICAL PROPERTIES | ||
| 1 | Mohs hardness * | > 6 | EN 101 |
| 2 | Abrasion resistance | >175 mm ³ | ISO-10545-6 |
| 3 | Skid Resistance (Friction Coefficient) | > 0.4 | ISO-10545-17 |
| E | CHEMICAL PROPERTIES | ||
| 1 | Frost resistance | Frost proof | ISO-10545-12 |
| 2 | Chemical Resistance | No Damage | ISO-10545-13 |
| 3 | Stain Resistance | Resistant | ISO-10545-14 |
| F | THERMAL PROPERTIES | ||
| 1 | Thermal Shock Resistance | No Damage | ISO-10545-9 |
| 2 | Thermal Expansion | < 9 x 10-6 | ISO-10545-8 |
| 3 | Moisture Expansion | Nil | ISO-10545-10 |
Η ακρίβεια διαστάσεων και η ποιότητα της επιφάνειας των πλακιδίων πορσελάνης διπλού φορτίου είναι απαραίτητες για τη διασφάλιση της ομοιομορφίας και της συνέπειας κατά τη διάρκεια της εγκατάστασης. Οι μέγιστες επιτρεπόμενες αποκλίσεις για το μήκος και το πάχος είναι ± 0,6% και ± 0,5% αντίστοιχα. Η ευθεία των πλευρών και οι αποκλίσεις της ορθογώνιας ορθοσταθμής καλύπτονται σε ± 0,5% και ± 0,6%. Η επιφάνεια της επιφάνειας πρέπει να παραμείνει σε ανοχή ± 0,5%, εξασφαλίζοντας ότι τα κεραμίδια βρίσκονται επίπεδη και ομαλή. Η γυαλιστερότητα, που μετράται με τη χρήση ενός μετρητή γυαλιστερού, εξασφαλίζει ότι το φινίρισμα της επιφάνειας πληροί τις αισθητικές και αντανακλαστικές απαιτήσεις.
Τα πλακάκια από πορσελάνη διπλής φόρτισης πρέπει να έχουν συγκεκριμένες δομικές ιδιότητες για να εξασφαλίσουν την ανθεκτικότητα και τις μακροπρόθεσμες επιδόσεις. Η απορρόφηση του νερού περιορίζεται κάτω από το 0,5%, καθιστώντας αυτά τα πλακάκια σχεδόν αδιαπέραστα και κατάλληλα για υγρά περιβάλλοντα. Μια πυκνότητα μεγαλύτερη από 2 g/cc υποδεικνύει τη στερεή και συμπαγή δομή των πλακιδίων, ενισχύοντας τη δύναμη και την ανθεκτικότητα τους.
Η μηχανική αντοχή των πλακιδίων πορσελάνης διπλού φορτίου είναι ζωτικής σημασίας για αντέκρου σε βαριά φορτία και πιέσεις. Η αντοχή στην κάμψη πρέπει να υπερβαίνει τα 27 N/mm2 και η αντοχή σπάσιμο πρέπει να φτάσει τουλάχιστον 1113 N. Αυτές οι ιδιότητες εξασφαλίζουν ότι τα κεραμίδια είναι ανθεκτικά στη ρωγμή και στο σπάσιμο, καθιστώντας τους ιδανικές τόσο για οικιακές όσο και για εμπορικές εφαρμογές που περιλαμβάνουν βαριά κυκλοφορία ή βάρος.
Τα κεραμίδια απαιτούνται για να παρουσιάσουν υψηλή αντοχή στην επιφάνεια σε διάφορες μηχανικές τάσεις. Μια βαθμολογία σκληρότητας MOHS άνω των 6 υποδεικνύει ισχυρή αντίσταση στο ξύσιμο, ενώ η αντίσταση στην τριβή πρέπει να είναι μεγαλύτερη από 175 mm³, εξασφαλίζοντας τη μακροζωία ακόμη και υπό συνθήκες υψηλής φθοράς. Ο συντελεστής τριβής πρέπει να είναι μεγαλύτερος από 0,4, παρέχοντας επαρκή αντίσταση ολίσθησης, απαραίτητη για την πρόληψη των γλίστρων και την εξασφάλιση της ασφάλειας σε περιοχές που εκτίθενται σε υγρασία ή συχνή κυκλοφορία ποδιών.
Οι χημικές ιδιότητες των πλακιδίων πορσελάνης διπλού φορτίου τους καθιστούν ιδιαίτερα ανθεκτικές σε εξωτερικές βλάβες από σκληρές περιβαλλοντικές συνθήκες. Αυτά τα κεραμίδια είναι απόδειξη του παγετού, καθιστώντας τα κατάλληλα για εγκατάσταση σε κρύα κλίματα. Είναι επίσης ανθεκτικά σε χημικά και λεκέδες, χωρίς βλάβη που εμφανίζεται μετά την έκθεση σε κοινές οικιακές χημικές ουσίες, εξασφαλίζοντας ότι η αισθητική και δομική ακεραιότητά τους διατηρείται με την πάροδο του χρόνου.
Αυτά τα πλακάκια είναι κατασκευασμένα για να αντισταθούν σε ζημιές από θερμικές αλλαγές. Η αντοχή σε θερμικό σοκ διασφαλίζει ότι τα κεραμίδια μπορούν να αντέξουν ξαφνικές αλλαγές στη θερμοκρασία χωρίς ρωγμές. Ο συντελεστής θερμικής διαστολής είναι μικρότερος από 9 x 10⁻⁶, ελαχιστοποιώντας τον κίνδυνο βλάβης που σχετίζεται με την επέκταση. Επιπλέον, τα κεραμίδια δεν δείχνουν επέκταση υγρασίας, εξασφαλίζοντας τη διαστασιακή σταθερότητα τους σε υγρά ή υγρά περιβάλλοντα.
| NO. | CHARACTERISTICS | REQUREMENT (AS PER ISO 13006 BIa / EN 176 BIa) | ISO / EN TESTING METHOD |
|---|---|---|---|
| A | DIMENSION & SURFACE QUALITY | ||
| 1 | Deviation In Length & Width | ± 0.60% | ISO-10545-2 |
| 2 | Deviation In Thickness | ± 5.00% | ISO-10545-2 |
| 3 | Straightness Of Sides | ± 0.50% | ISO-10545-2 |
| 4 | Rectangularity | ± 0.60% | ISO-10545-2 |
| 5 | Surface Flatness | ± 0.50% | ISO-10545-2 |
| 6 | Glosiness | ACCORDING TO SURFACE FINISH | GLOSSMETER |
| B | STRUCTURAL PROPERTIES | ||
| 1 | Water Absorption | ≤ 0.50% | ISO-10545-3 |
| 2 | Density (g/cc) | > 2 | DIN 51082 |
| C | MASSIVE MECHANICAL PROPERTIES | ||
| 1 | Flexural Strength * | > 35 N/mm ² | ISO-10545-4 |
| 2 | Breaking Strength | 1300 N | ISO-10545-4 |
| D | SURFACE MECHANICAL PROPERTIES | ||
| 1 | Moh’s Hardness | >6 | EN101 |
| 2 | Abrasion resistance | < 210 mm ³ | ISO-10545-6 |
| 3 | Skid Resistance (Friction Coefficient) | > 0.40 | ISO-10545-17 |
| E | CHEMICAL PROPERTIES | ||
| 1 | Frost Resistance | Frost Proof | ISO-10545-12 |
| 2 | Chemical Resistance | No Damage | ISO-10545-13 |
| 3 | Stain Resistance | Resistance | ISO-10545-14 |
| F | THERMAL PROPERTIES | ||
| 1 | Thermal Shock Resistance | No Damage | ISO-10545-9 |
| 2 | Thermal Expansion | < 9 x 10-6 | ISO-10545-8 |
| 3 | Moisture Expansion | Nil | ISO-10545-10 |
Η ακρίβεια διαστάσεων και η ποιότητα της επιφάνειας των πλακιδίων πορσελάνης πλήρους σώματος εξασφαλίζουν ομοιομορφία και εύκολη εγκατάσταση. Η απόκλιση του μήκους και του πλάτους περιορίζεται σε ± 0,60%και η μεταβολή του πάχους καλύπτεται σε ± 5,00%. Η ευθεία των πλευρών, η ορθογώνια και η επιφάνεια της επιφάνειας έχουν αυστηρές ανοχές ± 0,50% και ± 0,60% για να διατηρήσουν τη γεωμετρική ακρίβεια. Η στιλπνότητα μετράται σύμφωνα με το φινίρισμα της επιφάνειας χρησιμοποιώντας ένα μετρητή γυαλιστερού για να ικανοποιήσει τις αισθητικές απαιτήσεις.
Τα πλακάκια πορσελάνης πλήρους σώματος έχουν σχεδιαστεί για να έχουν ισχυρές δομικές ιδιότητες. Η απορρόφηση νερού διατηρείται σε ≤0,50%, εξασφαλίζοντας ότι είναι ιδιαίτερα ανθεκτικές στην υγρασία και κατάλληλα για χρήση σε υγρές περιοχές. Με πυκνότητα μεγαλύτερη από 2 g/cc, αυτά τα κεραμίδια είναι συμπαγή και ισχυρή, συμβάλλοντας στις μακροχρόνιες επιδόσεις τους σε περιβάλλοντα υψηλής κυκλοφορίας.
Η μηχανική αντοχή των πλακιδίων πορσελάνης πλήρους σώματος εξασφαλίζει ότι μπορούν να αντέξουν σημαντικά φορτία και πιέσεις χωρίς ρωγμές. Η αντοχή στην κάμψη υπερβαίνει τα 35 N/mm2 και η αντοχή θραύσης βαθμολογείται στο 1300 N, αποδεικνύοντας την ικανότητά τους να αντιστέκονται στις μεγάλες επιπτώσεις και να διατηρούν δομική ακεραιότητα σε απαιτητικές συνθήκες.
Αυτά τα κεραμίδια προσφέρουν ισχυρή αντίσταση στην επιφανειακή φθορά. Με βαθμολογία σκληρότητας MOHS μεγαλύτερη από 6, είναι ιδιαίτερα ανθεκτικές στο ξύσιμο. Η αντοχή τους σε τριβή μετράται σε <210 mm³, εξασφαλίζοντας ανθεκτικότητα σε περιοχές υψηλής κυκλοφορίας. Ένας συντελεστής αντίστασης σε ολισθαίνσεις> 0,40 εξασφαλίζει επαρκή τριβή για να αποτρέψει τα γλίστρες, καθιστώντας τους ασφαλείς για χρήση σε διάφορα περιβάλλοντα.
Τα πλακάκια πορσελάνης πλήρους σώματος παρουσιάζουν εξαιρετικές χημικές ιδιότητες, που είναι ανθεκτικές και ανθεκτικές σε βλάβες από χημική έκθεση. Η αντίσταση του παγετού τους καθιστά κατάλληλη για υπαίθριες εγκαταστάσεις σε κρύα κλίματα. Αντιμετωπίζουν επίσης τη χρώση και τη χημική βλάβη, διατηρώντας την εμφάνιση και τη λειτουργικότητά τους με την πάροδο του χρόνου.
Οι θερμικές ιδιότητες αυτών των πλακιδίων εξασφαλίζουν ότι μπορούν να αντέξουν τις διακυμάνσεις της θερμοκρασίας χωρίς βλάβη. Η αντοχή σε θερμικό σοκ διασφαλίζει ότι δεν εμφανίζεται ρωγμή όταν εκτίθεται σε ξαφνικές αλλαγές στη θερμοκρασία. Η θερμική επέκταση διατηρείται κάτω από 9 x 10 ⁻⁶, και τα κεραμίδια έχουν μηδενική επέκταση υγρασίας, παρέχοντας σταθερότητα και αξιοπιστία σε ποικίλες περιβαλλοντικές συνθήκες. Αυτές οι ιδιότητες κάνουν πλακάκια από πορσελάνη πλήρους σώματος πολύ ανθεκτικά τόσο για την εσωτερική όσο και για την εξωτερική χρήση.
| NO. | CHARACTERISTICS | REQUIREMENT (AS PER ISO-13006/EN14411 GROUP Bla) | ISO / EN TESTING METHOD |
|---|---|---|---|
| A | DIMENSION & SURFACE QUALITY | ||
| 1 | Deviation in length & width | ± 0.5% | ISO-10545-2 |
| 2 | Deviation in thickness | ± 5.0% | ISO-10545-2 |
| 3 | Straightness in side | ± 0.5% | ISO-10545-2 |
| 4 | Rectangularity | ± 0.5% | ISO-10545-2 |
| 5 | Surface flatness | ± 0.5% | ISO-10545-2 |
| 6 | Color difference | Unlterned | ISO-10545-16 |
| Glossiness | ACCORDING TO SURFACE FINISH | GLOSSOMETER | |
| B | STRUCTURAL PROPERTIES | ||
| 1 | Water Absorption | < 0.50% | ISO-10545-3 |
| 2 | Density (g/cc) | > 2.0 g/cc | DIN 51082 |
| C | MASSIVE MECHANICAL PROPERTIES | ||
| 1 | Modulus of repture | Min. 35 N/mm2 | ISO-10545-4 |
| 2 | Breaking strength | Min. 1300 N | ISO-10545-4 |
| 3 | Impact resistance | As per mfg. | ISO-10545-5 |
| D | SURFACE MECHANICAL PROPERTIES | ||
| 1 | Surface abrasion resistance | As per mfg. | ISO-10545-7 |
| 2 | MOH's hardness | As per mfg. | EN 101 |
| 3 | Skid Resistance (Friction Coefficient) | As per mfg. | ISO-10545-17 |
| E | CHEMICAL PROPERTIES | ||
| 1 | Frost Resistance | Frost Proof | ISO-10545-12 |
| 2 | Chemical Resistance | No Damage | ISO-10545-13 |
| 3 | Stain Resistance | Resistance | ISO-10545-14 |
| F | THERMAL PROPERTIES | ||
| 1 | Thermal Shock Resistance | No Damage | ISO-10545-9 |
| 2 | Thermal Expansion | < 9 x 10-6 | ISO-10545-8 |
| 3 | Moisture Expansion | Nil | ISO-10545-10 |
Τα πρότυπα διαστασιακής και επιφανειακής ποιότητας για την πορσελάνη GVT (υαλοειδείς πλακιδίων) εξασφαλίζουν υψηλή ακρίβεια και αισθητική τιμή. Οι αποκλίσεις στο μήκος και στο πλάτος ελέγχονται εντός ± 0,5%, ενώ οι μεταβολές πάχους περιορίζονται σε ± 5,0%. Η ευθεία, η ορθογώνια και η επιφάνεια της επιφάνειας διατηρούνται εντός ± 0,5%, εξασφαλίζοντας την ακριβή ευθυγράμμιση πλακιδίων κατά την εγκατάσταση. Η γυαλιστερότητα μετράται χρησιμοποιώντας μετρητή γυαλιστερού ανάλογα με το φινίρισμα της επιφάνειας και οι διαφορές χρώματος πρέπει να παραμείνουν αμετάβλητες για να διατηρηθούν η ομοιομορφία στην εμφάνιση.
Τα πλακάκια πορσελάνης GVT παρουσιάζουν ισχυρές δομικές ιδιότητες. Η απορρόφηση του νερού είναι μικρότερη από 0,50%, καθιστώντας αυτά τα πλακάκια ιδανικά για περιοχές που εκτίθενται σε υγρασία. Με πυκνότητα μεγαλύτερη από 2,0 g/cc, είναι συμπαγή και ανθεκτική, εξασφαλίζοντας μακροχρόνια απόδοση σε περιβάλλοντα υψηλής κυκλοφορίας και υψηλής υγρασίας.
Αυτά τα κεραμίδια διαθέτουν εντυπωσιακή μηχανική αντοχή, με συντελεστή ρήξης (αντοχή στην κάμψη) τουλάχιστον 35 n/mm2, υποδεικνύοντας υψηλή αντίσταση στην κάμψη και το στρες. Η αντοχή θραύσης βαθμολογείται σε τουλάχιστον 1300 N, γεγονός που εξασφαλίζει ότι τα κεραμίδια μπορούν να αντέξουν σημαντική πίεση χωρίς να σπάσουν. Η αντίσταση στην πρόσκρουση καθορίζεται από τον κατασκευαστή, επιβεβαιώνοντας περαιτέρω την ανθεκτικότητα των πλακιδίων σε προκλητικές συνθήκες.
Η αντίσταση στην τριβή της επιφάνειας, η σκληρότητα του MOHS και η αντίσταση ολίσθησης δοκιμάζονται με βάση τις προδιαγραφές του κατασκευαστή, εξασφαλίζοντας ότι τα πλακάκια πορσελάνης GVT διατηρούν την ακεραιότητα και την αντίσταση της επιφάνειας τους στην φθορά με την πάροδο του χρόνου. Αυτές οι ιδιότητες είναι ιδιαίτερα σημαντικές για τα πλακάκια που χρησιμοποιούνται σε περιοχές υψηλής κυκλοφορίας και για επιφάνειες που εκτίθενται σε συχνή τριβή.
Οι χημικές ιδιότητες των πλακιδίων πορσελάνης GVT τους καθιστούν εξαιρετικά ανθεκτικές και κατάλληλες τόσο για εσωτερική όσο και για εξωτερική χρήση. Είναι απόδειξη του παγετού, καθιστώντας τους ιδανικά για ψυχρότερα κλίματα. Αντιμετωπίζουν επίσης τη χημική βλάβη, δεν δείχνουν σημάδια φθοράς όταν εκτίθενται σε επιθετικές χημικές ουσίες. Η αντίσταση των λεκέδων τους εξασφαλίζει ότι η επιφάνεια παραμένει καθαρή και διατηρεί την αισθητική της έκκληση για μεγαλύτερες περιόδους.
Τα πλακάκια πορσελάνης GVT είναι ιδιαίτερα ανθεκτικά σε θερμικό σοκ, πράγμα που σημαίνει ότι δεν θα σπάσουν ή θα βλάψουν λόγω ταχείας μεταβολής της θερμοκρασίας. Ο συντελεστής θερμικής διαστολής διατηρείται κάτω από τα 9 x 10⁻⁶ και η επέκταση της υγρασίας είναι μηδενικός, εξασφαλίζοντας ότι τα πλακάκια διατηρούν το σχήμα και την ακεραιότητά τους ακόμη και σε κυμαινόμενες θερμοκρασίες ή περιβάλλοντα υψηλής υδατοσκεκτησίας. Αυτές οι θερμικές ιδιότητες τις καθιστούν κατάλληλες τόσο για εσωτερικές όσο και για εξωτερικές εγκαταστάσεις.
| NO. | CHARACTERISTICS | REQUIREMENT (AS PER ISO-13006/EN14411 GROUP Bla) | ISO / EN TESTING METHOD |
|---|---|---|---|
| A | DIMENSION & SURFACE QUALITY | ||
| 1 | Deviation in length & width | ± 0.6% | ISO-10545-2 |
| 2 | Deviation in thickness | ± 0.5% | ISO-10545-2 |
| 3 | Straightness in side | ± 0.5% | ISO-10545-2 |
| 4 | Rectangularity | ± 0.6% | ISO-10545-2 |
| 5 | Surface flatness | ± 0.5% | ISO-10545-2 |
| 6 | Glossiness | - | GLOSSOMETER |
| B | STRUCTURAL PROPERTIES | ||
| 1 | Water Absorption | < 0.50% | ISO-10545-3 |
| 2 | Density (g/cc) | > 2.0 g/cc | DIN 51082 |
| C | MASSIVE MECHANICAL PROPERTIES | ||
| 1 | Flexural Strength * | > 27 N/mm ² | ISO-10545-4 |
| 2 | Breaking Strength * | 1113 N | ISO-10545-4 |
| D | SURFACE MECHANICAL PROPERTIES | ||
| 1 | Mohs hardness * | > 6 | EN 101 |
| 2 | Abrasion resistance | >175 mm ³ | ISO-10545-6 |
| 3 | Skid Resistance (Friction Coefficient) | > 0.4 | ISO-10545-17 |
| E | CHEMICAL PROPERTIES | ||
| 1 | Frost resistance | Frost proof | ISO-10545-12 |
| 2 | Chemical Resistance | No Damage | ISO-10545-13 |
| 3 | Stain Resistance | Resistant | ISO-10545-14 |
| F | THERMAL PROPERTIES | ||
| 1 | Thermal Shock Resistance | No Damage | ISO-10545-9 |
| 2 | Thermal Expansion | < 9 x 10-6 | ISO-10545-8 |
| 3 | Moisture Expansion | Nil | ISO-10545-10 |
Η διαστασιακή και επιφανειακή ποιότητα των διαλυτών πλακιδίων πορσελάνης αλατιού εξασφαλίζει την ακρίβεια και την οπτική έκκληση. Οι αποκλίσεις στο μήκος και το πλάτος περιορίζονται σε ± 0,6%, ενώ η μεταβολή του πάχους ελέγχεται εντός ± 0,5%. Η ευθεία των πλευρών και η ορθογώνια διατηρείται εντός ± 0,5% και ± 0,6% αντίστοιχα, εξασφαλίζοντας την ομαλή εγκατάσταση. Η απόκλιση επιφανειακής επιφάνειας περιορίζεται σε ± 0,5%. Η στιλπνότητα της επιφάνειας πλακιδίων μετράται χρησιμοποιώντας ένα γυαλόμετρο.
Αυτά τα κεραμίδια έχουν εξαιρετικές δομικές ιδιότητες, καθιστώντας τα κατάλληλα για οικιακές και εμπορικές εφαρμογές. Η απορρόφηση του νερού είναι μικρότερη από 0,50%, γεγονός που εξασφαλίζει την ανθεκτικότητα σε υγρές συνθήκες. Η πυκνότητα είναι μεγαλύτερη από 2,0 g/cc, υποδεικνύοντας μια σταθερή και συμπαγή δομή, η οποία ενισχύει τη μακροζωία και τη συνολική απόδοση των πλακιδίων.
Τα διαλυτά πλακάκια από πορσελάνη αλατιού παρουσιάζουν σημαντική μηχανική αντοχή. Η αντοχή τους στην κάμψη είναι μεγαλύτερη από 27 N/mm², γεγονός που υποδεικνύει την ικανότητά τους να αντέχουν στην κάμψη χωρίς να σπάσουν. Η αντοχή θραύσης μετράται στο 1113 Ν, καθιστώντας τα ανθεκτικά σε βαριά φορτία και πίεση.
Οι επιφανειακές ιδιότητες είναι κρίσιμες για τις περιοχές που εκτίθενται σε υψηλή κυκλοφορία και φθορά. Τα κεραμίδια έχουν σκληρότητα MOHS μεγαλύτερη από 6, παρέχοντας ισχυρή αντίσταση στις γρατζουνιές και τις επιφανειακές βλάβες. Παρουσιάζουν αντίσταση τριβής μεγαλύτερη από 175 mm³, που σημαίνει ότι διατηρούν την ποιότητα της επιφάνειας τους για μεγαλύτερη διάρκεια. Η αντίσταση ολίσθησης (συντελεστής τριβής) είναι πάνω από 0,4, εξασφαλίζοντας μια ασφαλέστερη επιφάνεια για να περπατήσετε, ιδιαίτερα σε υγρές συνθήκες.
Οι χημικές ιδιότητες των πλακιδίων από πορσελάνη διαλυτού αλατιού εξασφαλίζουν την ανθεκτικότητα τους σε διαφορετικά περιβάλλοντα. Είναι απόδειξη του παγετού, καθιστώντας τους ιδανικά για κρύα κλίματα. Επίσης, παρουσιάζουν υψηλή αντίσταση στις χημικές ουσίες, που δείχνουν καμία βλάβη όταν εκτίθενται σε επιθετικές ουσίες. Η αντίσταση τους στη χρώση εξασφαλίζει ότι τα κεραμίδια διατηρούν την αισθητική τους έκκληση με την πάροδο του χρόνου, ακόμη και σε περιοχές επιρρεπείς σε διαρροές και βρωμιά.
Αυτά τα κεραμίδια προσφέρουν εξαιρετικές θερμικές ιδιότητες, καθιστώντας τα κατάλληλα για διαφορετικά κλίματα. Είναι ανθεκτικά σε θερμικό σοκ, που σημαίνει ότι δεν θα σπάσουν ή θα υποστούν βλάβη από ξαφνικές αλλαγές θερμοκρασίας. Ο συντελεστής θερμικής διαστολής είναι μικρότερος από 9 x 10⁻⁶ και δεν παρουσιάζουν επέκταση υγρασίας, εξασφαλίζοντας τη σταθερότητα διαστάσεων ακόμη και σε κυματοειδείς συνθήκες θερμοκρασίας και υγρασίας.
| NO. | CHARACTERISTICS | REQUIREMEN (As per 2556 (part I) 1994) |
|---|---|---|
| 1 | CRAZING TEST | No crazing up to 2 Cycle up to 5 hrs. Each Cycle up to 10 hrs. at pressure 0.34 to 0.37 Mps. |
| 2 | WATER ABSORPTION | Average Value should not exceed more than 0.5% |
| 3 | MODULUS OF REPTURE | Not less than 60 Mps. |
| 4 | CHEMICAL RESISTANCE | No less than of the glaze when compared with control sample |
| 5 | RESISTANCE TO STRAINING & BURNING | No stain shall remain on either of test piece |
| 6 | WAVY FINISH | None on all visible surface |
| 7 | DISCOLORATION | None on all visible surface |
Δοκιμή τρελών: Αυτή η δοκιμή αξιολογεί την ανθεκτικότητα του επιφανειακού λούστου κάτω από το στρες. Το υγειονομικό σκεύος δεν θα πρέπει να δείχνει καμία τρελή μετά από δύο κύκλους θεραπείας πίεσης - καθένα από τα οποία διαρκεί έως και πέντε ώρες και συνολικά δέκα ώρες σε πιέσεις μεταξύ 0,34 και 0,37 MPa.
Απορρόφηση νερού: Αυτή η προδιαγραφή υποδεικνύει τη μέγιστη επιτρεπόμενη απορρόφηση νερού του υλικού. Η μέση τιμή δεν πρέπει να υπερβαίνει το 0,5%, εξασφαλίζοντας ότι το προϊόν παραμένει ανθεκτικό στην υγρασία και διατηρεί τη δομική του ακεραιότητα.
Μέτρο ρήξης: Αυτή η ιδιοκτησία μετρά τη δύναμη των υγειονομικών ειδών. Το μέτρο ρήξης δεν πρέπει να είναι μικρότερο από 60 MPa, υποδεικνύοντας ότι το υλικό μπορεί να αντέξει σημαντική πίεση χωρίς σπάσιμο.
Χημική αντίσταση: Τα είδη υγιεινής πρέπει να παρουσιάζουν επαρκή αντίσταση στις χημικές ουσίες. Αυτή η απαίτηση διασφαλίζει ότι η ανθεκτικότητα του λούστου είναι συγκρίσιμη με ένα δείγμα ελέγχου, επιβεβαιώνοντας την ικανότητά του να αντέχει στην έκθεση σε διάφορες ουσίες χωρίς επιδείνωση.
Αντίσταση στη χρώση και καύση: Αυτό το χαρακτηριστικό αξιολογεί την ικανότητα της επιφάνειας να αντιστέκεται στους λεκέδες και στη θερμότητα. Δεν πρέπει να υπάρχει χρώση σε κανένα κομμάτι δοκιμής μετά την έκθεση σε συγκεκριμένες συνθήκες, υποδεικνύοντας την ανθεκτικότητα του προϊόντος και την ευκολία καθαρισμού.
Φινίρισμα: Το φινίρισμα του υγειονομικού σήματος θα πρέπει να είναι ομαλό, χωρίς κυματοδότηση σε οποιεσδήποτε ορατές επιφάνειες. Αυτό το κριτήριο εξασφαλίζει την αισθητική έκκληση και την πρακτική χρηστικότητα.
Αποχρωματισμός: Το υγειονομικό σκεύος δεν πρέπει να δείχνει αποχρωματισμό σε ορατές επιφάνειες. Αυτή η απαίτηση εγγυάται ότι το προϊόν διατηρεί την προβλεπόμενη εμφάνισή του με την πάροδο του χρόνου, ενισχύοντας την ικανοποίηση των πελατών και τη μακροζωία των προϊόντων.
| NO. | CHARACTERISTICS | STANDARD TEST | RESULT |
|---|---|---|---|
| 1 | APP. DENSITY KG/DM3 | EN14617-1 | 2.2-2.45 |
| 2 | WATER ABSORPTION | EN14617-1 | < 0.04 |
| 3 | FLEXURAL TRENGTH (MPA) | EN14617-2 | 50-60 |
| 4 | DIMENSIONAL STABILITY | EN14617-12 | CLASS A |
| 5 | IMPACT RESISTANCE (JOULE) | EN14617-9 | 4-9 JOULE |
| 6 | COMPRESSIVE STRENGTH (MPA) | EN14617-15 | 170-220 |
| 7 | ABRASION RESISTANCE | EN14617-4 | GROOVE LENGTH=21.1 MM |
| 8 | FROST RESISTANCE | DIN 52104 | COMPLIES WITH STANDARD |
| 9 | SURFACE HARDNESS (HOHS SCALE) | EN 101 | 6.0-7.0 |
| 10 | STAIN RESISTANCE | ANSI Z124.6 | PASS |
| 11 | WEAR & CLEANABILITY | ANSI Z124.6 | PASS |
| 12 | CHEMICAL RESISTANCE | ANSI Z124.6 | PASS |
| 13 | CHEMICAL RESISTANCE | EN14617-10 | CLASS C4 |
| 14 | RESISTANCE TO ACIDS | ASTM C 650 | NOT AFFECTED |
| 15 | LINEAR THERMAL EXPANSION (300-600) 0C-1 | EN14617-11 | 2.6x10-6 |
| 16 | BOILING WATER RESISTANCE | NEMA LD3-3.5 | PASS |
| 17 | HIGH TEMPERATURE RESISTANCE | NEMA LD3-3.6 | PASS |
| 18 | CIGARETTE TEST | ANSI Z124.6 | PASS |
| 19 | FIRE CLASSIFICATION | EN13501-1 | WALL CLADDING: B-S1-D0,FLOORING & STAIR: B-F1-S1 |
| 20 | SLIP RESISTANCE | EN 14231 | WET: 13-21 SRV, DRY: 43-53 SRV |
| 21 | REDIATION | GB 6566-2010 | COMPLIES WITH REQUIREMENT OF STANDARD |
| 22 | THERMAL SHOCK RESISTANCE | EN14617-6 | NO VISUAL DEFECTS AFTER 10 CYCLE |
| LOSS IN FLEXURAL STRENGTH = LOSS IN MASS = 0.02%-0.05% 0.07%-1.1% | |||
| 23 | FREEZE & THAW RESISTANCE | EN14617-5 | NO DEFECTS AFTER 25 FREEZE-THAW CYCLE |
| 24 | GLOSSINESS REFLECTION | % | 45-70 |
| 25 | SURFACE SLIP RESISTANCE HONED 400 | DIN 51130 | R9 |
| 26 | STATIC COEFFICIENT OF FRICTION | ASTM C 1028 | DRY: 0.8, WET: 0.6 |
Οι τεχνικές προδιαγραφές για το Quartz Stone περιλαμβάνουν διάφορα κρίσιμα χαρακτηριστικά που εξασφαλίζουν την ποιότητα, την ανθεκτικότητα και την καταλληλότητά της για διάφορες εφαρμογές. Η φαινομενική πυκνότητα κυμαίνεται από 2,2 έως 2,45 kg/dm³, υποδεικνύοντας την ισχυρή φυσική δομή της. Επιπλέον, η απορρόφηση του νερού είναι ελάχιστη, μετρούμενη σε λιγότερο από 0,04%, εξασφαλίζοντας ότι η πέτρα παραμένει αδιαπέραστη από την υγρασία. Η αντοχή της κάμψης κυμαίνεται μεταξύ 50 έως 60 MPa, αντανακλώντας την ικανότητά της να αντέχει τις δυνάμεις κάμψης, ενώ η αντοχή συμπίεσης φτάνει μεταξύ 170 και 220 MPa, υπογραμμίζοντας την αντοχή της κάτω από κατακόρυφα φορτία.
Άλλες σημαντικές δοκιμές περιλαμβάνουν αντίσταση στην τριβή, με μήκος αυλάκωσης 21,1 mm και αντίσταση στον παγετό, η οποία συμμορφώνεται με τα πρότυπα της βιομηχανίας. Το Quartz Stone επιδεικνύει επίσης εξαιρετική λεκέδες, φθορά και χημική αντίσταση, με αποτελέσματα που δεν δείχνουν ανεπιθύμητες ενέργειες. Επιπλέον, περνάει διάφορες δοκιμές θερμικής αντίστασης, συμπεριλαμβανομένης της αντοχής του νερού βρασμού και της αντοχής σε υψηλή θερμοκρασία. Συνολικά, αυτές οι προδιαγραφές επιβεβαιώνουν ότι το Quartz Stone είναι ένα ευπροσάρμοστο, ανθεκτικό υλικό κατάλληλο για αισθητικές και λειτουργικές εφαρμογές στην κατασκευή και το σχεδιασμό.