| NO. | CHARACTERISTICS | REQUREMENT (AS PER ISO 13006 BIa / EN 176 BI a) | ISO / EN TESTING METHOD |
|---|---|---|---|
| A | DIMENSION & SURFACE QUALITY | ||
| 1 | Deviation in Length & width | Max. +/- 0.5% | EN-98;IS:13630 (Part 1) |
| 2 | Deviation in thickness | Max. +/- 5% | EN-98;IS:13630 (Part 1) |
| 3 | Surface flatness (Warpage) | Max. +/- 0.5% | EN-98;IS:13630 (Part 1) |
| 4 | Rectangularity (Squareness) | Max. +/- 0.5% | EN-98;IS:13630 (Part 1) | B | PHYSICAL PROPERTIES |
| 1 | Water Absorption | >/= 10% | EN-99;IS:13630 (Part 2) |
| 2 | Scratch Hardness of Surface (Mohs) | Min. 3 | EN-101;IS:13630 (Part 13) |
| 3 | Resistance to Surface Abrasion (of tiles intended for use on floors) | Abration class shall be specified by the manufacturer | EN-154;IS:13630 (Part 11) |
| 4 | Crazing Resistance | Required | EN-105;IS:13630 (Part 9) |
| 5 | Modulus of Rupture | Min.153 Kg/cm2 | EN-100;IS:13630 (Part 6) | C | CHEMICAL / THERMAL PROPERTIES |
| 1 | STAINING RESISTANCE | MIN CLASS 2 | EN-122;IS:13630 (Part 8) |
| 2 | HOUSEHOLD CHEMICALS | MIN CLASS B | EN-122;IS:13630 (Part 8) |
| 3 | THERMAL SHOCK | RESISTANT TO 10 CYCLES | EN-104;IS:13630 (Part 5) |
| 4 | THERMAL EXPANSION | MAX-9E-06 | EN-104;IS:13630 (Part 5) |
Spesifikasi teknis kanggo jubin tembok digital adhedhasar ISO 13006 Bia / ing 176 bi. Iki dipérang dadi telung bagean utama: dimensi & kualitas lumahing, kualitas fisik, lan kimia / sifat termal.Bellow:
Dimensi & kualitas permukaan mesthekake yen kothak netepi standar khusus babagan syarat-syarat ukuran, bentuk, lan keseragaman lumahing. Penyebab sing bisa ditampa kanthi dawa, jembar, lan ketebalan kanthi ketat kanggo njaga konsistensi ing jubin. Miturut standar kasebut, jubin bisa duwe panyimpangan maksimal saka +/- 0,5% dawa lan jembaré, lan +/- 5% kanthi kekandelan. Kajaba iku, kothak kudu waras Warpage (Max +/- 0,5%) kanggo njamin flatness, lan mesthine alun-alun kanthi panyimpangan +/- 0,5% ing rectangularitas. Pangukuran kasebut penting kanggo jubin supaya pas kanthi bener sajrone diinstal lan njaga permukaan seragam kanthi visual.
Sipat fisik nemtokake kinerja jubin ing kahanan nyata-nyata, utamane nalika tundhuk stres fisik. Kaping pisanan, panyerepan banyu kudu ≥10%, sing nuduhake kepiye jubin kasebut lan cocog kanggo lingkungan sing beda-beda (penyerapan banyu sing luwih dhuwur ditemokake ing kothak tembok). Kekayaan pangripta permukaan, diukur ukuran moh, kudu paling ora 3, sing menehi ide babagan tilase tanduk yaiku kanggo ngeruk obyek umum. Jubin dimaksudake kanggo nggunakake lantai kudu nyukupi syarat resistensi abrasion, kanthi pabrikan nemtokake kelas abrasion. Tiles uga kudu tahan kanggo ngremehake (retak sing apik) ing kahanan normal. Pungkasane, modulus pecah (kemampuan jubin kanggo ngilangi) kudu paling sethithik 153 kg / cm², mesthekake jubin kasebut cukup kanggo ngatasi pasukan njaba.
Sifat kimia / termal nyorot resistensi jubin kanggo noda, bahan kimia, lan owah-owahan termal. Rintangan pewarnaan, kanthi syarat minimal saka kelas 2, mesthekake kothak kasebut bisa nahan cahya kanggo bahan-bahan rereget sing umum tanpa discolorasi permanen tanpa discolorasi permanen tanpa discolorasi permanen tanpa discolorasi permanen tanpa discolorasi permanen tanpa discolorasi permanen tanpa discolorasi permanen tanpa discolorasi permanen tanpa discolorasi permanen. Tiles uga kudu ngrusak karusakan saka bahan kimia kluwarga, diklasifikasikake kanthi minimal b, nggawe dheweke cocog kanggo pawon lan jedhing sing ana ing ngendi cahya kanggo ngresiki agen sing umum. Kanggo daya tahan termal, kothak kudu bisa nolak paling ora 10 siklus kejut termal, mesthekake yen bisa ngatasi owah-owahan suhu dadakan tanpa retak. Kajaba iku, koefision ekspansi termal ora kudu ngluwihi 9e-06, tegese jubin bakal mung nambah minimall nalika kapapar panas, njaga integritas struktural sajrone wektu.
| NO. | CHARACTERISTICS | REQUREMENT (AS PER ISO 13006 BIIa / EN 176 BII a) | ISO / EN TESTING METHOD | A | DIMENSION & SURFACE QUALITY |
|---|---|---|---|
| 1 | Deviation in Length & Width | ||
| a.The deviation in percent of the average size of each tile (2 or 4 sides) from the work size (w) | Max.± 0.6 | ISO-10545-2 IS:13630-1 | |
| b. The deviation in percent of the average size of each tile (2 or 4 sides) from the average size of the 10 test specimen (20 or 40 sides) | Max.± 0.5 | ISO-10545-2 IS:13630-1 | |
| 2 | Deviation in Thickness | Max.± 5.0% | ISO-10545-2 IS:13630-1 |
| 3 | Deviation in Straightness of sides | Max.±0.5% | ISO-10545-2 IS:13630-1 |
| 4 | Deviation in Rectangulanty | Max.±0.6% | ISO-10545-2 IS:13630-1 |
| 5 | Surface Flatness | ||
| a.Centre curvature (max.) | Max.± 0.5% | ISO-10545-2 IS:13630-1 | |
| b.Edge curvature (max.) | Max.± 0.5% | ISO-10545-2 IS:13630-1 | |
| c.Corner warpage (max.) | Max.± 0.5% | ISO-10545-2 IS:13630-1 | B | PHYSICAL PROPERTIES |
| 1 | Water Absorption | Avg.3 < E < 6% Individual max. 6.5% | ISO-10545-3 IS:13630-2 |
| 2 | Scratch Hardness (Moh's scale) | Not Required | IS:13630-13 |
| 3 | Abrasion Resistance | Tested as per PEI methodology | ISO-10545-7 IS:13630-11 |
| 4 | Crazing Resistance | Required | ISO-10545-11 IS:13630-9 |
| 5 | Modulus of Rupture in N/mm² | Avg. 22, Individual min 20 | ISO-10545-4 IS:13630-6 | C | CHEMICAL / THERMAL PROPERTIES |
| 1 | Chemical Resistance | Required,if agreed | ISO-10545-13 IS:13630-8 |
| 2 | Resistance to household chemicals | Class AA, min. | ISO-10545-13 IS:13630-8 |
| 3 | Resistance to staining | Class 1, min. | ISO-10545-14 IS:13630-8 |
| 4 | Thermal Shock | Required,if agreed | ISO-10545-9 IS:13630-5 |
Dimensi & kualitas permukaan negesake variasi sing diidini ing dimensi lan kualitas lumahing jubin keramik. Nyetel panyimpangan sing diidini maksimal kanthi dawa, jembar, lan kekandelan kanggo njamin keseragaman lan gampang instalasi. Panyimpangan kanthi dawa lan jembar dipérang dadi rong bagéan: siji sing mbandhingake ukuran jubin kasebut (maksimal panyimpangan ± 0.6%) lan ukuran maksimal saka ukuran ± 0,5 %). Perbandara maksimal kanthi kekandelan udakara ± 5%, mesthekake jubin kasebut konsisten ing kekandelan. Lurus sisi lan persagi diwatesi mung kanggo panyimpangan maksimal ± 0,5% lan ± 0.6%, masing-masing. Kajaba iku, lumahing flatness diukur kanthi kolokan tengah lan pinggiran uga warpage pojok, saben winates nganti ± 0,5% kanggo njamin permukaan sing lancar, sanajan permukaan.
Properti fisik nggambarake karakteristik fisik jubin, sing fokus ing panyerepan banyu, atose, lan kekuatan. Penyerapan banyu jubin keramik bisa kisaran ing antarane 3% lan 6%, kanthi maksimal 65%, supaya cocog kanggo lantai ing njero ruangan ing ngendi resistansi banyu penting. Kekayaan kesusahan, diukur ukuran moh, ora dibutuhake kanggo jubin lantai keramik. Rintangan abrasion diuji nggunakake cara pei, sing njamin kothak bisa tahan lalu lintas sikil. Rintangan kepinginan wajib, mesthekake jubin ora bakal ngembangake retak sing luwih suwe. Modulus pecah, sing ngukur kekuatan jubin, kudu duwe nilai rata-rata 22 N / MM², kanthi nilai individu minimal saka 20 N / MM² minimal, nuduhake bisa nangani tekanan sing sadurunge bubar.
Sifat kimia / termal ngevaluasi resistensi kothak kanggo bahan kimia, pewarnaan, lan kejut termal. Jubin kasebut kudu tahan kimia, utamane yen syarat iki disepakati karo pabrikan. Dheweke uga duwe resistensi AA paling ora kelas kanggo bahan kimia kluwarga, tegese bisa nahan cahya kanggo agen pembersihan umum tanpa rusak. Rintangan sing paling murah sing dibutuhake kanggo pewarna yaiku kelas 1, mesthekake jubin tetep resik lan ora ana ing panggunaan biasa. Rintangan kejut termal dibutuhake yen wis ditemtokake, mesthekake yen kothak bisa tahan owah-owahan suhu dadakan tanpa retak, sing penting kanggo kothak sing digunakake ing lingkungan sing digunakake ing lingkungan sing digunakake ing lingkungan sing digunakake ing lingkungan sing digunakake ing lingkungan sing digunakake ing lingkungan sing digunakake ing lingkungan sing digunakake ing lingkungan sing digunakake ing lingkungan sing digunakake ing lingkungan sing digunakake ing lingkungan sing digunakake ing lingkungan sing digunakake ing lingkungan sing digunakake ing lingkungan sing digunakake ing lingkungan sing digunakake ing lingkungan sing digunakake ing lingkungan sing digunakake ing lingkungan sing digunakake ing lingkungan sing digunakake ing lingkungan sing digunakake ing lingkungan sing digunakake ing lingkungan sing digunakake ing lingkungan sing digunakake ing lingkungan sing digunakake ing lingkungan sing digunakake ing lingkungan sing digunakake ing lingkungan sing digunakake ing lingkungan sing digunakake ing lingkungan sing digunakake ing lingkungan sing digunakake ing lingkungan sing digunakake ing lingkungan sing digunakake ing lingkungan sing digunakake ing lingkungan sing digunakake ing lingkungan sing digunakake ing lingkungan sing digunakake ing lingkungan sing digunakake ing lingkungan sing digunakake ing lingkungan sing digunakake ing lingkungan sing digunakake ing lingkungan sing digunakake ing lingkungan sing digunakake ing lingkungan sing digunakake ing lingkungan sing digunakake ing lingkungan sing digunakake ing lingkungan sing digunakake.
| NO. | CHARACTERISTICS | REQUREMENT (AS PER ISO 13006 BIa / EN 176 BIa) | ISO / EN TESTING METHOD |
|---|---|---|---|
| A | DIMENSION & SURFACE QUALITY | ||
| 1 | Deviation in length | ± 0.6% | ISO-10545-2 |
| 2 | Deviation in thickness | ± 5.0% | ISO-10545-2 |
| 3 | Straightness of sides | ± 0.5% | ISO-10545-2 |
| 4 | Rectangularity | ± 0.6% | ISO-10545-2 |
| B | PHYSICAL PROPERTIES | ||
| 1 | Water absorption | <0.5% | ISO-10545-2 |
| 2 | MOH's hardness | >6 | EN101 |
| 3 | Flexural strength | >35 N/mm2 | ISO-10545-4 |
| 4 | Abrasion resistance | <175mm3 | ISO-10545-6 |
| 5 | Breaking strength | 1113N | ISO-10545-6 |
| Density (gm/cc) | >2 | ISO-10545-3 | |
| C | CHEMICAL / THERMAL PROPERTIES | ||
| 1 | Frost resistance | Frostproof | ISO-10545-12 |
| 2 | Chemical resistance | No damage | ISO-10545-13 |
| 3 | Thermal shock resistance | No damage | ISO-10545-9 |
| 4 | Colour resistance | No damage | DIN 51094 |
| 5 | Thermal expansion | < 9 x 10-6 | ISO-10545-8 |
| 6 | Stain resistance | Resistance | ISO-10545-14 |
| 7 | Moisture expansion | Nil | ISO-10545-10 |
Dimensi & kualitas permukaan negesake variasi dimensi kothak sing diidini kanggo kothak parkir, njamin konsistensi lan akurasi produksi. Dawane jubin bisa nyimpang kanthi maksimal ± 0,6%, lan kekandelanane kanthi ± 5.0%. Lurus sisi lan persagi diwatesi kanggo panyimpangan ± 0,5% lan ± 0.6%, sing mbantu njaga keseragaman sajrone instalasi. Toleransi iki kritis kanggo alignment sing tepat lan pas, mesthine jubin kasebut nyedhiyakake permukaan sing lancar lan stabil cocog kanggo wilayah lalu lintas sing dhuwur.
Sifat fisik saka jubin parkir penting kanggo kinerja ing lingkungan ruangan. Penyerapan banyu kudu ana ing ngisor 0,5%, mesthekake jubin tahan tahan kanggo kelembapan lan cocog kanggo kahanan teles utawa udan. Jubin uga kudu nuduhake peringkat athi atose luwih saka 6, nuduhake yen tahan banget kanggo ngeruk. Kekuwatan fleksibal kudu ngluwihi 35 n / mm², tegese jubin bisa nahan pasukan pambengkongane, nalika resistensi abrasion kudu kurang saka 175mm³, mesthekake yen bisa nyemprotake sing tetep saka kendaraan lan lalu lintas sikil. Kekuwatan mecah kudu tekan 1113n, njamin kothak kasebut awet ing beban abot. Kapadhetan Tiles kudu luwih saka 2 g / cm³, nggambarake konstruksi padhet lan kapasitas kanggo tahan stres.
Tiles parkir kudu bisa nahan kahanan lingkungan sing atos, kalebu cahya kimia lan fluktuasi suhu. Jubin kasebut tahan Frost, nggawe dheweke cocog kanggo iklim sing luwih adhem. Dheweke uga bisa ngrusak karusakan saka bahan kimia lan kejut termal, njamin umur dawa sanajan kena kahanan sing ekstrem. Rintangan warna mesthekake yen kothak njaga penampilan sajrone wektu, sanajan cahya srengenge utawa panas. Ekspansi termal diwatesi kurang saka 9 X 10º, tegese jubin ora bakal nggedhekake owah-owahan suhu, njaga integritas struktural. Dheweke uga bisa nolak reregetan lan ekspansi kelembapan, mesthekake yen dheweke tetep resik lan stabil ing macem-macem kahanan cuaca.
| NO. | CHARACTERISTICS | REQUREMENT (AS PER ISO 13006 BIa / EN 176 BIa) | ISO / EN TESTING METHOD |
|---|---|---|---|
| A | DIMENSION & SURFACE QUALITY | ||
| 1 | Deviation in Length | ± 0.6% | ISO-10545-2 |
| 2 | Deviation in Thickness | ± 0.5% | ISO-10545-2 |
| 3 | Straightness of Sides | ± 0.5% | ISO-10545-2 |
| 4 | Rectangularity | ± 0.6% | ISO-10545-2 |
| 5 | Surface Flatness | ± 0.5% | ISO-10545-2 |
| 6 | Glosiness | - | GLOSSMETER |
| B | STRUCTURAL PROPERTIES | ||
| 1 | Water absorption * | < 0.5% | ISO-10545-3 |
| 2 | Density (g/cc) | > 2 | DIN 51082 |
| C | MASSIVE MECHANICAL PROPERTIES | ||
| 1 | Flexural Strength * | > 27 N/mm ² | ISO-10545-4 |
| 2 | Breaking Strength * | 1113 N | ISO-10545-4 |
| D | SURFACE MECHANICAL PROPERTIES | ||
| 1 | Mohs hardness * | > 6 | EN 101 |
| 2 | Abrasion resistance | >175 mm ³ | ISO-10545-6 |
| 3 | Skid Resistance (Friction Coefficient) | > 0.4 | ISO-10545-17 |
| E | CHEMICAL PROPERTIES | ||
| 1 | Frost resistance | Frost proof | ISO-10545-12 |
| 2 | Chemical Resistance | No Damage | ISO-10545-13 |
| 3 | Stain Resistance | Resistant | ISO-10545-14 |
| F | THERMAL PROPERTIES | ||
| 1 | Thermal Shock Resistance | No Damage | ISO-10545-9 |
| 2 | Thermal Expansion | < 9 x 10-6 | ISO-10545-8 |
| 3 | Moisture Expansion | Nil | ISO-10545-10 |
Akurasi Dimensional lan kualitas lumahing saka jubin porsin dobel sing penting kanggo mesthekake keseragaman lan konsistensi sajrone instalasi. Penyebab utama sing diidini maksimal kanggo dawa lan kekandelan udakara ± 0.6% lan ± 05%. Lurus sisi lan panyimpangan persegi dipasang ing ± 0,5% lan ± 0.6%. Lumahing flatness kudu tetep ing toleransi ± 0,5%, njamin kothak layel lancar. Kelayakan, diukur nggunakake meter gloss, mesthekake lumahing lumahing bisa nyukupi syarat estetika lan reflektif.
Jubin porsel sing dobel kudu duwe sifat struktural khusus kanggo njamin kekiatan lan kinerja jangka panjang. Penyerapan banyu diwatesi ing ngisor 0,5%, nggawe jubin kasebut meh ora bisa ditrapake lan cocog kanggo lingkungan sing teles. Kapadhetan luwih saka 2 g / cc nuduhake struktur padhet lan kompak jubatan jubin, nambah kekuwatane lan daya tahan.
Kekuwatan mekanik saka jubin porsel sing dobel penting kanggo akeh beban lan tekanan sing abot. Kekuwatan fleksibal kudu ngluwihi ukuran 27 n / mm², lan kekuatan mecah paling ora 1113 n. Properti kasebut mesthekake yen kothak kasebut tahan kanggo rempah-rempah lan bejat sing beda karo lalu lintas utawa bobote.
Jubin kasebut dibutuhake kanggo nampilake resistensi permukaan sing dhuwur kanggo macem-macem stres mekanik. Rating keras moh luwih saka 6 nuduhake resistensi sing kuwat kanggo ngeruk, amarga tahan abrasion kudu luwih saka 175 mm³, njamin umur dawa. Koefisial gesekan kudu luwih saka 0,4, nyedhiyakake resistensi skid sing cukup, penting kanggo nyegah slip lan njamin keamanan sing ana kelembapan utawa lalu lintas sikil.
Sifat kimia saka jubin porsel sing dobel nggawe dheweke tahan kanggo karusakan eksternal saka kahanan lingkungan sing atos. Jubin kasebut minangka bukti Frost, nggawe dheweke cocog kanggo nginstal ing iklim kadhemen. Dheweke uga tahan kanggo bahan kimia lan rereged, tanpa karusakan sing kedadeyan sawise cahya kanggo bahan kimia kluwarga umum, mesthekake integritas estetika lan struktural sing disimpen.
Jubin kasebut dipasang kanggo nolak karusakan saka owah-owahan termal. Rintangan kejut termal mesthekake yen kothak bisa terus owah-owahan suhu kanthi cepet tanpa retak. Koeisi ekspansi termal kurang saka 9 X 10º, minimalake risiko karusakan sing gegandhengan karo ekspansi. Kajaba iku, jubin ora nuduhake ekspansi kelembapan, njamin stabilitas dimensi ing lingkungan sing lembab utawa teles.
| NO. | CHARACTERISTICS | REQUREMENT (AS PER ISO 13006 BIa / EN 176 BIa) | ISO / EN TESTING METHOD |
|---|---|---|---|
| A | DIMENSION & SURFACE QUALITY | ||
| 1 | Deviation In Length & Width | ± 0.60% | ISO-10545-2 |
| 2 | Deviation In Thickness | ± 5.00% | ISO-10545-2 |
| 3 | Straightness Of Sides | ± 0.50% | ISO-10545-2 |
| 4 | Rectangularity | ± 0.60% | ISO-10545-2 |
| 5 | Surface Flatness | ± 0.50% | ISO-10545-2 |
| 6 | Glosiness | ACCORDING TO SURFACE FINISH | GLOSSMETER |
| B | STRUCTURAL PROPERTIES | ||
| 1 | Water Absorption | ≤ 0.50% | ISO-10545-3 |
| 2 | Density (g/cc) | > 2 | DIN 51082 |
| C | MASSIVE MECHANICAL PROPERTIES | ||
| 1 | Flexural Strength * | > 35 N/mm ² | ISO-10545-4 |
| 2 | Breaking Strength | 1300 N | ISO-10545-4 |
| D | SURFACE MECHANICAL PROPERTIES | ||
| 1 | Moh’s Hardness | >6 | EN101 |
| 2 | Abrasion resistance | < 210 mm ³ | ISO-10545-6 |
| 3 | Skid Resistance (Friction Coefficient) | > 0.40 | ISO-10545-17 |
| E | CHEMICAL PROPERTIES | ||
| 1 | Frost Resistance | Frost Proof | ISO-10545-12 |
| 2 | Chemical Resistance | No Damage | ISO-10545-13 |
| 3 | Stain Resistance | Resistance | ISO-10545-14 |
| F | THERMAL PROPERTIES | ||
| 1 | Thermal Shock Resistance | No Damage | ISO-10545-9 |
| 2 | Thermal Expansion | < 9 x 10-6 | ISO-10545-8 |
| 3 | Moisture Expansion | Nil | ISO-10545-10 |
Akurasi dimensi lan kualitas permukaan jubin porsel porcelain awak lengkap njamin keseragaman lan instalasi gampang. Penyebaran ing dawa lan jembaré diwatesi mung ± 0,60%, lan variasi ketebalan dicelupake ing ± 5.00%. Sakcedhake sisih, persegionalitas, lan lumahing flatness duwe toleransi sing ketat saka ± 0,50% lan ± 0.60% kanggo njaga tliti geometrik. Geloskan diukur miturut lumahing rampung nggunakake meter gloss kanggo nyukupi syarat estetika.
Jubin porselin awak lengkap dirancang kanggo duwe sifat struktural sing kuwat. Penyerapan banyu disimpen kanggo ≤0.50%, mesthekake yen tahan kelembapan lan cocog kanggo digunakake ing wilayah udan. Kanthi kapadhetan luwih saka 2 g / cc, jubin kasebut kompak lan mantep, menehi kontribusi sing dawa ing lingkungan lalu lintas dhuwur.
Kekuwatan mekanik saka jubin porselin awak lengkap sing bisa nahan akeh beban lan tekanan sing signifikan tanpa retak. Kekuwatan flextural ngluwihi 35 n / mm², lan kekuatan mecah dibiji ing 1300 n, nuduhake kemampuan kanggo nolak pengaruh sing abot lan njaga integritas struktural ing kahanan sing nuntut.
Jubin kasebut nawakake resistensi sing kuwat kanggo nyandhang lumahing lan luh. Kanthi rating atos mohwelas luwih saka 6, dheweke tahan banget kanggo ngeruk. Rintangan abrasi sing diukur ing <210 mm³, mesthekake kekiatan ing wilayah lalu lintas dhuwur. Koefisi resistensi Skid ing> 0.40 njamin gesekan sing cukup kanggo nyegah slip, supaya bisa digunakake ing macem-macem lingkungan.
Jubin porcelain awak lengkap nuduhake sipat kimia sing apik banget, dadi Frost-bukti lan tahan karusakan saka cahya kimia. Rintangan Frost nggawe dheweke cocog kanggo instalasi ruangan ing iklim adhem. Dheweke uga nolak pewarnaan lan karusakan kimia, njaga tampilan lan fungsine luwih suwe.
Sifat termal saka kothak iki mesthekake bisa nahan fluktuasi suhu tanpa rusak. Rintangan kejut termal mesthekake yen ora ana cracking nalika kena owah-owahan suhu. Ekspansi termal tetep ing ngisor 9 x 10⁻⁶, lan jubin kasebut duwe ekspansi kelembapan nul, nyedhiyakake stabilitas lan linuwih ing macem-macem kahanan lingkungan. Properti kasebut nggawe jubin porselain awak lengkap kanthi tahan lama kanggo panggunaan njero ruangan lan ruangan.
| NO. | CHARACTERISTICS | REQUIREMENT (AS PER ISO-13006/EN14411 GROUP Bla) | ISO / EN TESTING METHOD |
|---|---|---|---|
| A | DIMENSION & SURFACE QUALITY | ||
| 1 | Deviation in length & width | ± 0.5% | ISO-10545-2 |
| 2 | Deviation in thickness | ± 5.0% | ISO-10545-2 |
| 3 | Straightness in side | ± 0.5% | ISO-10545-2 |
| 4 | Rectangularity | ± 0.5% | ISO-10545-2 |
| 5 | Surface flatness | ± 0.5% | ISO-10545-2 |
| 6 | Color difference | Unlterned | ISO-10545-16 |
| Glossiness | ACCORDING TO SURFACE FINISH | GLOSSOMETER | |
| B | STRUCTURAL PROPERTIES | ||
| 1 | Water Absorption | < 0.50% | ISO-10545-3 |
| 2 | Density (g/cc) | > 2.0 g/cc | DIN 51082 |
| C | MASSIVE MECHANICAL PROPERTIES | ||
| 1 | Modulus of repture | Min. 35 N/mm2 | ISO-10545-4 |
| 2 | Breaking strength | Min. 1300 N | ISO-10545-4 |
| 3 | Impact resistance | As per mfg. | ISO-10545-5 |
| D | SURFACE MECHANICAL PROPERTIES | ||
| 1 | Surface abrasion resistance | As per mfg. | ISO-10545-7 |
| 2 | MOH's hardness | As per mfg. | EN 101 |
| 3 | Skid Resistance (Friction Coefficient) | As per mfg. | ISO-10545-17 |
| E | CHEMICAL PROPERTIES | ||
| 1 | Frost Resistance | Frost Proof | ISO-10545-12 |
| 2 | Chemical Resistance | No Damage | ISO-10545-13 |
| 3 | Stain Resistance | Resistance | ISO-10545-14 |
| F | THERMAL PROPERTIES | ||
| 1 | Thermal Shock Resistance | No Damage | ISO-10545-9 |
| 2 | Thermal Expansion | < 9 x 10-6 | ISO-10545-8 |
| 3 | Moisture Expansion | Nil | ISO-10545-10 |
Standar kualitas dimensi lan permukaan kanggo GVT (jubin vitrified) porselin njamin nilai sing tliti lan estetika. Dawane dawane lan jembaré dikendhaleni ing ± 0,5%, nalika variasi ketebalan diwatesi mung ± 5.0%. Sakcedhake, persegi panjang, lan lumahing flatness kabeh disimpen ing ± 0,5%, njamin alignment kothak akurat sajrone instalasi. Glossiness diukur nggunakake meter gloss gumantung saka lumahing lumahing, lan bedane warna kudu tetep ora kaleren kanggo njaga keseragaman.
Jubin porselin Gvt nuduhake kualitas struktural struktural. Penyerapan banyu kurang saka 0,50%, nggawe jubin kasebut cocog kanggo wilayah sing ana kelembapan. Kanthi kapadhetan luwih saka 2.0 g / cc, padha kompak lan kuat, njamin kinerja sing dawa lan lingkungan sing luwih lembab lan dhuwur.
Jubin kasebut nduwe kekuwatan mekanik sing nggumunake, kanthi modulus pecah (kekuatan fleksibal) paling ora 35 n / mm², nuduhake resistensi dhuwur kanggo mbengkongake lan stres. Kekuwatan mecah dibiji kanthi minimal 1300 n, sing njamin jubin bisa nahan tekanan sing signifikan tanpa rusak. Rintangan pengaruh ditemtokake dening pabrikan, luwih ngonfirmasi kekiatan saka kothak kanthi kahanan tantangan.
Rintangan abrasium lumahing, keras moh, lan tahan skid diuji adhedhasar spesifikasi pabrikan, mesthekake yen kothak lan resistensi permukaan GVT njaga lan nyuwek wektu. Sifat-sifat kasebut penting banget kanggo jubin sing digunakake ing wilayah lalu lintas dhuwur lan kanggo permukaan sing ana gesekan.
Sifat-sifat kimia saka jubin porselin GVT nggawe dheweke awet lan cocog kanggo panggunaan njero ruangan lan ruangan. Dheweke dadi bukti Frost, dadi luwih becik kanggo iklim sing luwih adhem. Dheweke uga nolak karusakan bahan kimia, sing ora nuduhake tandha-tandha nalika kapapar bahan kimia sing agresif. Rintangan kehakiman sing njamin permukaan tetep resik lan njaga banding estetika kanggo wektu sing luwih suwe.
Jubin porselin GVT tahan banget kanggo kejut termal, tegese dheweke ora bakal ngremehake utawa ngrusak amarga owah-owahan suhu kanthi cepet. Koeisi ekspansi termal dijaga ing ngisor iki 9 X 10º, lan ekspansi kelembapan yaiku NIL, yen kothak kasebut njaga wujud lan integritas sing ana ing suhu sing asor utawa lingkungan sing asor. Properti termal kasebut nggawe dheweke cocog kanggo instalasi njero ruangan lan ruangan.
| NO. | CHARACTERISTICS | REQUIREMENT (AS PER ISO-13006/EN14411 GROUP Bla) | ISO / EN TESTING METHOD |
|---|---|---|---|
| A | DIMENSION & SURFACE QUALITY | ||
| 1 | Deviation in length & width | ± 0.6% | ISO-10545-2 |
| 2 | Deviation in thickness | ± 0.5% | ISO-10545-2 |
| 3 | Straightness in side | ± 0.5% | ISO-10545-2 |
| 4 | Rectangularity | ± 0.6% | ISO-10545-2 |
| 5 | Surface flatness | ± 0.5% | ISO-10545-2 |
| 6 | Glossiness | - | GLOSSOMETER |
| B | STRUCTURAL PROPERTIES | ||
| 1 | Water Absorption | < 0.50% | ISO-10545-3 |
| 2 | Density (g/cc) | > 2.0 g/cc | DIN 51082 |
| C | MASSIVE MECHANICAL PROPERTIES | ||
| 1 | Flexural Strength * | > 27 N/mm ² | ISO-10545-4 |
| 2 | Breaking Strength * | 1113 N | ISO-10545-4 |
| D | SURFACE MECHANICAL PROPERTIES | ||
| 1 | Mohs hardness * | > 6 | EN 101 |
| 2 | Abrasion resistance | >175 mm ³ | ISO-10545-6 |
| 3 | Skid Resistance (Friction Coefficient) | > 0.4 | ISO-10545-17 |
| E | CHEMICAL PROPERTIES | ||
| 1 | Frost resistance | Frost proof | ISO-10545-12 |
| 2 | Chemical Resistance | No Damage | ISO-10545-13 |
| 3 | Stain Resistance | Resistant | ISO-10545-14 |
| F | THERMAL PROPERTIES | ||
| 1 | Thermal Shock Resistance | No Damage | ISO-10545-9 |
| 2 | Thermal Expansion | < 9 x 10-6 | ISO-10545-8 |
| 3 | Moisture Expansion | Nil | ISO-10545-10 |
Kualitas dimensi lan permukaan larut larut larut larut njamin presisi lan banding visual. Nyimpang kanthi dawa lan jembaré diwatesi kanthi ± 0,6%, nalika variasi ketebalan dikontrol ing ± 0,5%. Lancar lan secara langsung lan persegionalitas disimpen ing ± 0,5% lan ± 0,6% masing-masing, njamin instalasi lancar. Penyebaran Flatness Surface diwatesi nganti ± 0,5%. Glosks saka permukaan kothak diukur nggunakake glossometer.
Jubin kasebut duwe sifat struktural sing apik, nggawe dheweke cocog kanggo aplikasi omah lan komersial. Penyerapan banyu kurang saka 0,50%, sing njamin ketahanan ing kahanan lembab. Kapadhetan kasebut luwih saka 2.0 g / cc, nuduhake struktur sing padhet lan kompak, sing nambah umur dawa lan umure kothak.
Jubin porcelain uyah sing larut nuduhake kekuwatan mekanik sing signifikan. Kekuwatan flexural dheweke luwih saka 27 n / mm², sing nuduhake kemampuan kanggo nahan bendah tanpa bejat. Kekuwatan mecah diukur ing 1113 n, nggawe dheweke bisa nyebabake akeh lan tekanan.
Proses lumahing kritis kanggo wilayah sing kapapar lalu lintas dhuwur lan nyandhang. Jubin duwe kekerasan moh sing luwih saka 6, nyedhiyakake resistensi sing kuwat kanggo goresan lan karusakan lumahing. Dheweke nampilake tahan abrasion luwih saka 175 mm³, tegese bisa nahan kualitas permukaan sajrone luwih suwe. Rintangan skid (koefisi gesekan) luwih dhuwur 0,4, njamin permukaan sing luwih aman kanggo mlaku-mlaku, utamane ing kahanan udan.
Properti kimia larut jubin uyah larut njamin ketahanan ing lingkungan sing beda. Dheweke dadi bukti Frost, nggawe dheweke cocog kanggo iklim adhem. Dheweke uga nuduhake resistensi sing dhuwur kanggo bahan kimia, nuduhake ora ngrusak nalika kapapar zat sing agresif. Rintangan dheweke kanggo ngresiki manawa jubin njaga banding estetika sajrone wektu, sanajan ing wilayah sing gampang diluncurake lan rereget.
Jubin kasebut nawakake sipat termal sing apik, nggawe dheweke cocog kanggo macem-macem iklim. Dheweke tahan kanggo kejut termal, tegese dheweke ora bakal retak utawa rusak amarga owah-owahan suhu dadakan. Koeisi ekspansi termal kurang saka 9 X 10º, lan ora nuduhake ekspansi kelembapan, njamin stabilitas dimensi sanajan ing kahanan asor.
| NO. | CHARACTERISTICS | REQUIREMEN (As per 2556 (part I) 1994) |
|---|---|---|
| 1 | CRAZING TEST | No crazing up to 2 Cycle up to 5 hrs. Each Cycle up to 10 hrs. at pressure 0.34 to 0.37 Mps. |
| 2 | WATER ABSORPTION | Average Value should not exceed more than 0.5% |
| 3 | MODULUS OF REPTURE | Not less than 60 Mps. |
| 4 | CHEMICAL RESISTANCE | No less than of the glaze when compared with control sample |
| 5 | RESISTANCE TO STRAINING & BURNING | No stain shall remain on either of test piece |
| 6 | WAVY FINISH | None on all visible surface |
| 7 | DISCOLORATION | None on all visible surface |
Tes crazing: Tes iki netepke daya tahan saka permukaan permukaan ing stres. Ware kebersihan kudu ora nuduhake sawise ngalami rong siklus tekanan - saben nganti limang jam, lan udakara sepuluh jam ing tekanan ing antarane 0,34 nganti 0.37 MPA.
Penyerapan banyu: Spesifikasi iki nuduhake penyerapan banyu sing diidini maksimal. Nilai rata-rata ora kudu ngluwihi 0,5%, mesthekake yen produk tetep tahan kelembapan lan njaga integritas struktural.
Modulus pecah: Properti iki ngukur kekuatan ware kebersihan. Modulus pecah kudu kurang saka 60 MPA, nuduhake manawa materi bisa tahan stres sing signifikan tanpa rusak.
Rintangan kimia: Wira kebersihan kudu menehi resistensi sing cukup kanggo bahan kimia. Keperluan iki njamin kekiatan cemlorot dibandhingake karo conto kontrol, konfirmasi kemampuan kanggo tahan cahya kanggo macem-macem bahan tanpa rusak.
Rintangan kanggo ngresiki & ngobong: Karakteristik iki ngevaluasi kemampuan permukaan kanggo nolak rereged lan panas. Mesthi ora ana pewarnaan ing potongan tes sawise eksposisi kanggo kahanan sing ditemtokake, sing nuduhake daya tahan lan gampang ngresiki.
Wangi rampung: Rampung saka ware kebersihan kudu lancar, tanpa tundhuk ing permukaan sing katon. Kriteri iki njamin banding estetika lan panggunaan praktis.
Discoloration: Ware kebersihan ora kudu nuduhake discolorasi ing permukaan sing katon. Keperluan iki njamin manawa produk kasebut nahan tampilan sing dimaksud sajrone wektu, nambah kepuasan pelanggan lan umur dawa.
| NO. | CHARACTERISTICS | STANDARD TEST | RESULT |
|---|---|---|---|
| 1 | APP. DENSITY KG/DM3 | EN14617-1 | 2.2-2.45 |
| 2 | WATER ABSORPTION | EN14617-1 | < 0.04 |
| 3 | FLEXURAL TRENGTH (MPA) | EN14617-2 | 50-60 |
| 4 | DIMENSIONAL STABILITY | EN14617-12 | CLASS A |
| 5 | IMPACT RESISTANCE (JOULE) | EN14617-9 | 4-9 JOULE |
| 6 | COMPRESSIVE STRENGTH (MPA) | EN14617-15 | 170-220 |
| 7 | ABRASION RESISTANCE | EN14617-4 | GROOVE LENGTH=21.1 MM |
| 8 | FROST RESISTANCE | DIN 52104 | COMPLIES WITH STANDARD |
| 9 | SURFACE HARDNESS (HOHS SCALE) | EN 101 | 6.0-7.0 |
| 10 | STAIN RESISTANCE | ANSI Z124.6 | PASS |
| 11 | WEAR & CLEANABILITY | ANSI Z124.6 | PASS |
| 12 | CHEMICAL RESISTANCE | ANSI Z124.6 | PASS |
| 13 | CHEMICAL RESISTANCE | EN14617-10 | CLASS C4 |
| 14 | RESISTANCE TO ACIDS | ASTM C 650 | NOT AFFECTED |
| 15 | LINEAR THERMAL EXPANSION (300-600) 0C-1 | EN14617-11 | 2.6x10-6 |
| 16 | BOILING WATER RESISTANCE | NEMA LD3-3.5 | PASS |
| 17 | HIGH TEMPERATURE RESISTANCE | NEMA LD3-3.6 | PASS |
| 18 | CIGARETTE TEST | ANSI Z124.6 | PASS |
| 19 | FIRE CLASSIFICATION | EN13501-1 | WALL CLADDING: B-S1-D0,FLOORING & STAIR: B-F1-S1 |
| 20 | SLIP RESISTANCE | EN 14231 | WET: 13-21 SRV, DRY: 43-53 SRV |
| 21 | REDIATION | GB 6566-2010 | COMPLIES WITH REQUIREMENT OF STANDARD |
| 22 | THERMAL SHOCK RESISTANCE | EN14617-6 | NO VISUAL DEFECTS AFTER 10 CYCLE |
| LOSS IN FLEXURAL STRENGTH = LOSS IN MASS = 0.02%-0.05% 0.07%-1.1% | |||
| 23 | FREEZE & THAW RESISTANCE | EN14617-5 | NO DEFECTS AFTER 25 FREEZE-THAW CYCLE |
| 24 | GLOSSINESS REFLECTION | % | 45-70 |
| 25 | SURFACE SLIP RESISTANCE HONED 400 | DIN 51130 | R9 |
| 26 | STATIC COEFFICIENT OF FRICTION | ASTM C 1028 | DRY: 0.8, WET: 0.6 |
Spesifikasi teknis kanggo watu kuarz kalebu macem-macem karakteristik kritis sing njamin kekiatan, lan cocog kanggo macem-macem aplikasi. Kapadhetan sing jelas kalebu udakara 2,2 nganti 2,45 kg / dm³, nuduhake struktur fisik sing kuat. Kajaba iku, panyerepan banyu minimal, diukur kurang saka 0,04%, njamin watu tetep ora ana kelembapan. Kekuwatan fleksibal ing antarane 50 nganti 60 MPA, nggambarake kemampuane kanggo nahan pasukan lengkeh, dene kekuatan kompresif tekan antarane 170 nganti 220 MPA, negesake kekuwatane ing lebar vertikal.
Tes sing penting liyane kalebu resistensi abrasion, kanthi dawane alur 21,1 mm, lan resistensi Frost, sing tundhuk karo standar industri. Kuarsa Watu uga nduduhake noda sing apik, nyandhang, lan resistensi kimia, kanthi asil sing nuduhake efek mbebayani. Kajaba iku, ngliwati macem-macem tes ketahanan termal, kalebu resistensi banyu lan resistensi suhu dhuwur. Sakabèhé, spesifikasi kasebut konfirmasi manawa watu kuarza kasebut minangka bahan serbaguna, bahan tahan lama sing cocog kanggo aplikasi estetika lan fungsional ing konstruksi lan desain.