| NO. | CHARACTERISTICS | REQUREMENT (AS PER ISO 13006 BIa / EN 176 BI a) | ISO / EN TESTING METHOD |
|---|---|---|---|
| A | DIMENSION & SURFACE QUALITY | ||
| 1 | Deviation in Length & width | Max. +/- 0.5% | EN-98;IS:13630 (Part 1) |
| 2 | Deviation in thickness | Max. +/- 5% | EN-98;IS:13630 (Part 1) |
| 3 | Surface flatness (Warpage) | Max. +/- 0.5% | EN-98;IS:13630 (Part 1) |
| 4 | Rectangularity (Squareness) | Max. +/- 0.5% | EN-98;IS:13630 (Part 1) |
| B | PHYSICAL PROPERTIES | ||
| 1 | Water Absorption | >/= 10% | EN-99;IS:13630 (Part 2) |
| 2 | Scratch Hardness of Surface (Mohs) | Min. 3 | EN-101;IS:13630 (Part 13) |
| 3 | Resistance to Surface Abrasion (of tiles intended for use on floors) | Abration class shall be specified by the manufacturer | EN-154;IS:13630 (Part 11) |
| 4 | Crazing Resistance | Required | EN-105;IS:13630 (Part 9) |
| 5 | Modulus of Rupture | Min.153 Kg/cm2 | EN-100;IS:13630 (Part 6) |
| C | CHEMICAL / THERMAL PROPERTIES | ||
| 1 | STAINING RESISTANCE | MIN CLASS 2 | EN-122;IS:13630 (Part 8) |
| 2 | HOUSEHOLD CHEMICALS | MIN CLASS B | EN-122;IS:13630 (Part 8) |
| 3 | THERMAL SHOCK | RESISTANT TO 10 CYCLES | EN-104;IS:13630 (Part 5) |
| 4 | THERMAL EXPANSION | MAX-9E-06 | EN-104;IS:13630 (Part 5) |
Digitaalsete seinaplaatide tehnilised spetsifikatsioonid, mis põhinevad ISO 13006 BIA / EN 176 BI A standardid. See jaguneb kolmeks peamiseks osaks: mõõde ja pinna kvaliteet, füüsikalised omadused ja keemilised / termilised omadused.
Mõõde ja pinna kvaliteet tagab, et plaadid kleepuvad konkreetsete standardite järgi suuruse, kuju ja pinna ühtluse osas. Pikkuse pikkuse, laiuse ja paksuse vastuvõetavad kõrvalekalded on rangelt reguleeritud, et säilitada konsistents plaatide vahel. Standardite kohaselt võib plaatide pikkuse ja laiuse maksimaalne kõrvalekalle olla +/- 0,5% ning +/- 5% paksus. Lisaks peab plaatidel olema minimaalne lõime (max +/- 0,5%), et tagada tasasus, ja need peaksid olema ruudukujulised, vastuvõetava kõrvalekaldega +/- 0,5% ristkülikukujulises. Need mõõtmised on üliolulised, et plaadid sobiksid paigaldamise ajal korralikult ja säilitada visuaalselt ühtlase pinna.
Füüsikalised omadused määratlevad plaatide jõudluse reaalsetes tingimustes, eriti kui füüsiline stress. Esiteks peab vee imendumine olema ≥10%, mis näitab, kui poorne plaat on, ja selle sobivus erinevatele keskkondadele (seinaplaatides leidub tavaliselt suurem vee imendumine). MOHS -i skaalal mõõdetud pinna kriimustus karadus peab olema vähemalt 3, mis annab aimu, kui vastupidav on plaat tavalistest objektidest kriimustamisele. Põranda kasutamiseks mõeldud plaadid peavad vastama hõõrdumiskindluse nõuetele, tootja täpsustab hõõrdumisklassi. Plaadid peavad olema ka normaalsetes tingimustes vastupidavad (peen pragunemine). Lõpuks peab rebenemismoodul (plaadi võime pidada purunemist) olema vähemalt 153 kg/cm², tagades, et plaadid on väliste jõudude käitlemiseks piisavalt tugevad.
Keemilised / termilised omadused rõhutavad plaatide vastupidavust plekkide, kemikaalide ja termiliste muutuste suhtes. Värvimiskindlus koos 2. klassi minimaalse nõudega tagab, et plaadid taluvad kokkupuudet tavaliste värvimisvahenditega ilma püsiva värvuseta. Plaadid peavad vastu pidama ka majapidamiskemikaalide kahjustustele, mis on klassifitseeritud vähemalt B -klassis, muutes need sobivaks köökidele ja vannitubadele, kus puhastusvahenditega kokkupuude on tavaline. Termilise vastupidavuse tagamiseks peavad plaadid olema võimelised seisma vastu vähemalt 10 termilise šoki tsüklile, tagades, et nad saavad temperatuuri järskude muutustega hakkama ilma pragunemata. Lisaks ei tohi soojuspaisumistegur ületada 9E-06, mis tähendab, et plaadid laienevad kuumusega kokkupuutel vaid minimaalselt, säilitades aja jooksul nende konstruktsiooni terviklikkuse.
| NO. | CHARACTERISTICS | REQUREMENT (AS PER ISO 13006 BIIa / EN 176 BII a) | ISO / EN TESTING METHOD |
|---|---|---|---|
| A | DIMENSION & SURFACE QUALITY | ||
| 1 | Deviation in Length & Width | ||
| a.The deviation in percent of the average size of each tile (2 or 4 sides) from the work size (w) | Max.± 0.6 | ISO-10545-2 IS:13630-1 | |
| b. The deviation in percent of the average size of each tile (2 or 4 sides) from the average size of the 10 test specimen (20 or 40 sides) | Max.± 0.5 | ISO-10545-2 IS:13630-1 | |
| 2 | Deviation in Thickness | Max.± 5.0% | ISO-10545-2 IS:13630-1 |
| 3 | Deviation in Straightness of sides | Max.±0.5% | ISO-10545-2 IS:13630-1 |
| 4 | Deviation in Rectangulanty | Max.±0.6% | ISO-10545-2 IS:13630-1 |
| 5 | Surface Flatness | ||
| a.Centre curvature (max.) | Max.± 0.5% | ISO-10545-2 IS:13630-1 | |
| b.Edge curvature (max.) | Max.± 0.5% | ISO-10545-2 IS:13630-1 | |
| c.Corner warpage (max.) | Max.± 0.5% | ISO-10545-2 IS:13630-1 | |
| B | PHYSICAL PROPERTIES | ||
| 1 | Water Absorption | Avg.3 < E < 6% Individual max. 6.5% | ISO-10545-3 IS:13630-2 |
| 2 | Scratch Hardness (Moh's scale) | Not Required | IS:13630-13 |
| 3 | Abrasion Resistance | Tested as per PEI methodology | ISO-10545-7 IS:13630-11 |
| 4 | Crazing Resistance | Required | ISO-10545-11 IS:13630-9 |
| 5 | Modulus of Rupture in N/mm² | Avg. 22, Individual min 20 | ISO-10545-4 IS:13630-6 |
| C | CHEMICAL / THERMAL PROPERTIES | ||
| 1 | Chemical Resistance | Required,if agreed | ISO-10545-13 IS:13630-8 |
| 2 | Resistance to household chemicals | Class AA, min. | ISO-10545-13 IS:13630-8 |
| 3 | Resistance to staining | Class 1, min. | ISO-10545-14 IS:13630-8 |
| 4 | Thermal Shock | Required,if agreed | ISO-10545-9 IS:13630-5 |
Mõõt ja pinna kvaliteet kirjeldab keraamiliste põrandaplaatide mõõtmete ja pinnakvaliteedi lubatud erinevusi. See seab maksimaalse lubatud kõrvalekalde pikkuse, laiuse ja paksuse, et tagada paigaldamise ühtlus ja lihtsus. Pikkuse ja laiuse kõrvalekalle jaguneb kaheks osaks: üks, mis võrdleb plaadi suurust töösuurusega (maksimaalne kõrvalekalle ± 0,6%) ja teine, mis võrdleb plaadi suurust katseproovide keskmise suurusega (maksimaalne kõrvalekalle ± 0,5 %). Paksuse maksimaalne kõrvalekalle on ± 5%, tagades, et plaadid on nende paksuses ühtlased. Külgede sirge ja ristkülikukujulisus piirdub maksimaalse kõrvalekallega vastavalt ± 0,5% ja ± 0,6%. Lisaks mõõdetakse pinna lamedust keskpunkti ja serva kumerusega, samuti nurga lõimega, mis igaüks on ± 0,5%, et tagada sile, ühtlane pind.
Füüsikalised omadused kirjeldavad plaatide füüsilisi omadusi, keskendudes vee imendumisele, kõvadusele ja tugevusele. Keraamiliste põrandaplaatide vee imendumine peab olema vahemikus 3–6%, individuaalse maksimaalselt 6,5%, mis muudab need sobivaks siseruumides, kus veekindlus on hädavajalik. MOHS -i skaalal mõõdetud kriimustus kõvadus pole keraamiliste põrandaplaatide jaoks vajalik. Hõõrumiskindlust testitakse PEI meetodi abil, mis tagab, et plaadid taluvad jalgade liiklust. Hoolustamiskindlus on kohustuslik, tagades, et plaadid ei tekiks aja jooksul peeneid pragusid. Plaatide tugevust mõõdetava rebenemismooduli keskmine väärtus peaks olema 22 N/mm², minimaalse individuaalse väärtusega 20 N/mm², mis näitab, et nad saavad enne purunemist märkimisväärse survega hakkama saada.
Keemilised / termilised omadused hindavad plaatide vastupidavust kemikaalidele, värvimisele ja termilisele šokile. Plaadid peaksid olema keemiliselt vastupidavad, eriti kui see nõue on tootjaga kokku lepitud. Neil peab olema ka vähemalt klassi AA resistentsus leibkonna kemikaalidele, mis tähendab, et nad taluvad kokkupuudet tavaliste puhastusvahenditega ilma lagunemiseta. Minimaalne nõutav vastupidavus värvimisele on 1. klass, tagades, et plaadid püsivad regulaarses kasutamises puhtaks ja viimistlemata. Kui täpsustatakse, on vajalik termiline löögikindlus, tagades, et plaadid võivad temperatuuri järskude muutusi ilma pragunemiseta, mis on oluline kõikuva temperatuuriga keskkondades kasutatavate plaatide jaoks.
| NO. | CHARACTERISTICS | REQUREMENT (AS PER ISO 13006 BIa / EN 176 BIa) | ISO / EN TESTING METHOD |
|---|---|---|---|
| A | DIMENSION & SURFACE QUALITY | ||
| 1 | Deviation in length | ± 0.6% | ISO-10545-2 |
| 2 | Deviation in thickness | ± 5.0% | ISO-10545-2 |
| 3 | Straightness of sides | ± 0.5% | ISO-10545-2 |
| 4 | Rectangularity | ± 0.6% | ISO-10545-2 |
| B | PHYSICAL PROPERTIES | ||
| 1 | Water absorption | <0.5% | ISO-10545-2 |
| 2 | MOH's hardness | >6 | EN101 |
| 3 | Flexural strength | >35 N/mm2 | ISO-10545-4 |
| 4 | Abrasion resistance | <175mm3 | ISO-10545-6 |
| 5 | Breaking strength | 1113N | ISO-10545-6 |
| Density (gm/cc) | >2 | ISO-10545-3 | |
| C | CHEMICAL / THERMAL PROPERTIES | ||
| 1 | Frost resistance | Frostproof | ISO-10545-12 |
| 2 | Chemical resistance | No damage | ISO-10545-13 |
| 3 | Thermal shock resistance | No damage | ISO-10545-9 |
| 4 | Colour resistance | No damage | DIN 51094 |
| 5 | Thermal expansion | < 9 x 10-6 | ISO-10545-8 |
| 6 | Stain resistance | Resistance | ISO-10545-14 |
| 7 | Moisture expansion | Nil | ISO-10545-10 |
Mõõde ja pinna kvaliteet kirjeldab parkimisplaatide lubatud mõõtmete variatsioone, tagades nende tootmise järjepidevuse ja täpsuse. Plaatide pikkus võib erineda maksimaalselt ± 0,6%ja nende paksus ± 5,0%. Külgede ja ristkülikukujulisuse sirged piirduvad vastavalt ± 0,5% ja ± 0,6%, mis aitab paigaldamise ajal ühtlust säilitada. Need tolerantsid on kriitilise tähtsusega õigeks joondamiseks ja sobivaks, tagades, et plaadid pakuvad sujuvat ja stabiilset pinda, mis sobib kõrge liiklusega piirkondadele, näiteks parklate jaoks.
Parkimisplaatide füüsikalised omadused on üliolulised nende jõudluseks õues keskkonnas. Vee imendumine peab olema alla 0,5%, tagades, et plaadid on niiskuse suhtes väga vastupidavad ja sobivad niisketele või vihmastele tingimustele. Plaatidel peab olema ka MOHS -i kõvadusreiting suurem kui 6, mis näitab, et need on kriimustustele väga vastupidavad. Paindetugevus peab ületama 35 N/mm², mis tähendab, et plaadid taluvad paindejõude, samas kui hõõrdumiskindlus peaks olema väiksem kui 175 mm³, tagades, et need suudavad sõidukite ja jalaliikluse pidevat kulumist taluda. Korraldustugevus peab jõudma 1113n -ni, tagades, et plaadid on vastupidavad raskete koormuste all. Plaatide tihedus peab olema suurem kui 2 g/cm³, kajastades nende tahket konstruktsiooni ja stressi talumise võimekust.
Parkimisplaadid peavad olema võimelised taluma karme keskkonnatingimusi, sealhulgas keemilist kokkupuudet ja temperatuuri kõikumisi. Plaadid on külmakindlad, muutes need sobivaks külmemaks kliimaks. Samuti peavad nad vastu pidama kemikaalide ja termilise šoki kahjustustele, tagades pikaealisuse isegi ekstreemsete tingimustega kokkupuutel. Värvikutakistus tagab, et plaadid säilitavad aja jooksul oma välimuse, vaatamata kokkupuutele päikesevalgusele või kuumusele. Termiline laienemine on piiratud alla 9 x 10⁻⁶, mis tähendab, et plaadid ei laiene temperatuurimuutustega märkimisväärselt, säilitades konstruktsiooni terviklikkuse. Samuti peavad nad vastu plekkidele ja niiskuse laienemisele, tagades, et need jäävad erinevates ilmastikutingimustes puhtaks ja stabiilseks.
| NO. | CHARACTERISTICS | REQUREMENT (AS PER ISO 13006 BIa / EN 176 BIa) | ISO / EN TESTING METHOD |
|---|---|---|---|
| A | DIMENSION & SURFACE QUALITY | ||
| 1 | Deviation in Length | ± 0.6% | ISO-10545-2 |
| 2 | Deviation in Thickness | ± 0.5% | ISO-10545-2 |
| 3 | Straightness of Sides | ± 0.5% | ISO-10545-2 |
| 4 | Rectangularity | ± 0.6% | ISO-10545-2 |
| 5 | Surface Flatness | ± 0.5% | ISO-10545-2 |
| 6 | Glosiness | - | GLOSSMETER |
| B | STRUCTURAL PROPERTIES | ||
| 1 | Water absorption * | < 0.5% | ISO-10545-3 |
| 2 | Density (g/cc) | > 2 | DIN 51082 |
| C | MASSIVE MECHANICAL PROPERTIES | ||
| 1 | Flexural Strength * | > 27 N/mm ² | ISO-10545-4 |
| 2 | Breaking Strength * | 1113 N | ISO-10545-4 |
| D | SURFACE MECHANICAL PROPERTIES | ||
| 1 | Mohs hardness * | > 6 | EN 101 |
| 2 | Abrasion resistance | >175 mm ³ | ISO-10545-6 |
| 3 | Skid Resistance (Friction Coefficient) | > 0.4 | ISO-10545-17 |
| E | CHEMICAL PROPERTIES | ||
| 1 | Frost resistance | Frost proof | ISO-10545-12 |
| 2 | Chemical Resistance | No Damage | ISO-10545-13 |
| 3 | Stain Resistance | Resistant | ISO-10545-14 |
| F | THERMAL PROPERTIES | ||
| 1 | Thermal Shock Resistance | No Damage | ISO-10545-9 |
| 2 | Thermal Expansion | < 9 x 10-6 | ISO-10545-8 |
| 3 | Moisture Expansion | Nil | ISO-10545-10 |
Topeltlaengu portselanist plaatide mõõtmete täpsus ja pinnakvaliteet on paigaldamise ajal ühtluse ja järjepidevuse tagamiseks hädavajalikud. Maksimaalsed lubatud pikkuse ja paksuse kõrvalekalded on vastavalt ± 0,6% ja ± 0,5%. Külgede sirge ja ristkülikulisuse kõrvalekalded piirduvad ± 0,5% ja ± 0,6%. Pinna tasasus peab püsima tolerantsi piires ± 0,5%, tagades, et plaadid on lamedad ja siledad. Läikivarvestusega mõõdetud läikivus tagab, et pinna viimistlus vastab esteetilistele ja peegeldavatele nõuetele.
Topeltlaengu portselanist plaatidel peavad olema spetsiifilised struktuurilised omadused, et tagada vastupidavus ja pikaajaline jõudlus. Vee imendumine on piiratud alla 0,5%, muutes need plaadid peaaegu läbitungimatuks ja sobivaks niiskeks keskkonnaks. Tihedus üle 2 g/cm3 näitab plaatide tahket ja kompaktset struktuuri, suurendades nende tugevust ja vastupidavust.
Topeltlaenguga portselanist plaatide mehaaniline tugevus on raskete koormuste ja rõhkude vastu pidamiseks ülioluline. Paindlik tugevus peab ületama 27 N/mm² ja purunemisjõud peaks ulatuma vähemalt 1113 N. Need omadused tagavad, et plaadid on pragunemisele ja purunemisele vastupidavad, muutes need ideaalseks nii elamu- kui ka kaubanduslike rakenduste jaoks, mis hõlmavad tihedat liiklust või kaalu.
Plaadid on vajalikud kõrge pinnatakistuse ilmnemiseks mitmesuguste mehaaniliste pingete suhtes. MOHS -i kõvadusreiting üle 6 näitab tugevat vastupidavust kriimustumisele, samas kui hõõrdumiskindlus peab olema suurem kui 175 mm³, tagades pikaealisuse isegi kõrgetes kulumistingimustes. Hõõrdekoefitsient peab olema suurem kui 0,4, pakkudes piisavat libisemiskindlust, mis on hädavajalik libisemiste ennetamiseks ja ohutuse tagamiseks niiskuse või sagedase jalaliikluse korral.
Topeltlaenguga portselanist plaatide keemilised omadused muudavad need karmide keskkonnatingimuste väliste kahjustuste suhtes väga vastupidavaks. Need plaadid on külmakindlad, muutes need sobivaks külma kliimaga paigaldamiseks. Need on ka kemikaalide ja plekkide suhtes vastupidavad, pärast tavaliste leibkonna kemikaalidega kokkupuudet ei tekkinud kahju, tagades, et nende esteetiline ja struktuurne terviklikkus säilitatakse aja jooksul.
Need plaadid on konstrueeritud, et takistada termiliste muutuste kahjustusi. Termiline löögikindlus tagab, et plaadid võivad temperatuuri järskude muutusi ilma pragudeta taluda. Soojuspaisumistegur on väiksem kui 9 x 10⁻⁶, minimeerides laienemisega seotud kahjustuste riski. Lisaks ei näita plaadid niiskuse laienemist, tagades nende mõõtmete stabiilsuse niiskes või niisketes keskkondades.
| NO. | CHARACTERISTICS | REQUREMENT (AS PER ISO 13006 BIa / EN 176 BIa) | ISO / EN TESTING METHOD |
|---|---|---|---|
| A | DIMENSION & SURFACE QUALITY | ||
| 1 | Deviation In Length & Width | ± 0.60% | ISO-10545-2 |
| 2 | Deviation In Thickness | ± 5.00% | ISO-10545-2 |
| 3 | Straightness Of Sides | ± 0.50% | ISO-10545-2 |
| 4 | Rectangularity | ± 0.60% | ISO-10545-2 |
| 5 | Surface Flatness | ± 0.50% | ISO-10545-2 |
| 6 | Glosiness | ACCORDING TO SURFACE FINISH | GLOSSMETER |
| B | STRUCTURAL PROPERTIES | ||
| 1 | Water Absorption | ≤ 0.50% | ISO-10545-3 |
| 2 | Density (g/cc) | > 2 | DIN 51082 |
| C | MASSIVE MECHANICAL PROPERTIES | ||
| 1 | Flexural Strength * | > 35 N/mm ² | ISO-10545-4 |
| 2 | Breaking Strength | 1300 N | ISO-10545-4 |
| D | SURFACE MECHANICAL PROPERTIES | ||
| 1 | Moh’s Hardness | >6 | EN101 |
| 2 | Abrasion resistance | < 210 mm ³ | ISO-10545-6 |
| 3 | Skid Resistance (Friction Coefficient) | > 0.40 | ISO-10545-17 |
| E | CHEMICAL PROPERTIES | ||
| 1 | Frost Resistance | Frost Proof | ISO-10545-12 |
| 2 | Chemical Resistance | No Damage | ISO-10545-13 |
| 3 | Stain Resistance | Resistance | ISO-10545-14 |
| F | THERMAL PROPERTIES | ||
| 1 | Thermal Shock Resistance | No Damage | ISO-10545-9 |
| 2 | Thermal Expansion | < 9 x 10-6 | ISO-10545-8 |
| 3 | Moisture Expansion | Nil | ISO-10545-10 |
Terve keha portselanist plaatide mõõtmete täpsus ja pinnakvaliteet tagavad ühtluse ja hõlpsa paigaldamise. Pikkuse ja laiuse kõrvalekalle on piiratud ± 0,60%ja paksuse variatsioon on piiratud ± 5,00%. Külgede, ristkülikukujulise ja pinna tasapinna sirged on geomeetrilise täpsuse säilitamiseks ranged tolerantsid ± 0,50% ja ± 0,60%. Läikikut mõõdetakse vastavalt pinnaviimistlusele, kasutades esteetilistele nõuetele läikivarvesti.
Kogu keha portselanist plaadid on loodud tugevate struktuuriliste omadustega. Vee imendumine hoitakse ≤0,50%, tagades, et need on niiskuse suhtes väga vastupidavad ja sobivad kasutamiseks niisketes kohtades. Kuna tihedus on suurem kui 2 g/cm3, on need plaadid kompaktsed ja vastupidavad, aidates kaasa pikaajalisele jõudlusele kõrge liiklusega keskkonnas.
Terve keha portselanist plaatide mehaaniline tugevus tagab, et need taluvad olulist koormust ja rõhku ilma pragunemata. Paindetugevus ületab 35 N/mm² ja purunemis tugevus on hinnatud 1300 n juures, mis näitab nende võimet seista vastu rasketele mõjudele ja säilitada nõudlikes tingimustes konstruktsiooni terviklikkust.
Need plaadid pakuvad tugevat vastupidavust pinna kulumisele. Kuna MoHS -i kõvadusreiting on suurem kui 6, on need kriimustustele väga vastupidavad. Nende kulumiskindlust mõõdetakse <210 mm³, tagades vastupidavuse kõrge liiklusega piirkondades. Libisemiskordaja> 0,40 tagab libisemise vältimiseks piisava hõõrdumise, muutes need erinevates keskkondades kasutamiseks ohutuks.
Kogu keha portselanist plaatidel on suurepärased keemilised omadused, mis on külmakindlad ja vastupidavad keemilise kokkupuute kahjustustele. Külmakindlus muudab need sobivaks külma kliimas asuvateks välitingimustes. Samuti seisavad nad vastu värvimisele ja keemilistele kahjustustele, säilitades oma välimuse ja funktsionaalsuse aja jooksul.
Nende plaatide termilised omadused tagavad, et need taluvad temperatuuri kõikumisi ilma kahjustusteta. Termiline löögikindlus tagab, et temperatuuri äkiliste muutuste kokkupuutel ei toimu pragunemist. Soojuspaisumist hoitakse alla 9 x 10⁻⁶ ja plaatidel on niiskuse laienemine null, pakkudes stabiilsust ja usaldusväärsust erinevates keskkonnatingimustes. Need omadused muudavad kogu keha portselanist plaadid väga vastupidavaks nii sise- kui ka välistingimustes kasutamiseks.
| NO. | CHARACTERISTICS | REQUIREMENT (AS PER ISO-13006/EN14411 GROUP Bla) | ISO / EN TESTING METHOD |
|---|---|---|---|
| A | DIMENSION & SURFACE QUALITY | ||
| 1 | Deviation in length & width | ± 0.5% | ISO-10545-2 |
| 2 | Deviation in thickness | ± 5.0% | ISO-10545-2 |
| 3 | Straightness in side | ± 0.5% | ISO-10545-2 |
| 4 | Rectangularity | ± 0.5% | ISO-10545-2 |
| 5 | Surface flatness | ± 0.5% | ISO-10545-2 |
| 6 | Color difference | Unlterned | ISO-10545-16 |
| Glossiness | ACCORDING TO SURFACE FINISH | GLOSSOMETER | |
| B | STRUCTURAL PROPERTIES | ||
| 1 | Water Absorption | < 0.50% | ISO-10545-3 |
| 2 | Density (g/cc) | > 2.0 g/cc | DIN 51082 |
| C | MASSIVE MECHANICAL PROPERTIES | ||
| 1 | Modulus of repture | Min. 35 N/mm2 | ISO-10545-4 |
| 2 | Breaking strength | Min. 1300 N | ISO-10545-4 |
| 3 | Impact resistance | As per mfg. | ISO-10545-5 |
| D | SURFACE MECHANICAL PROPERTIES | ||
| 1 | Surface abrasion resistance | As per mfg. | ISO-10545-7 |
| 2 | MOH's hardness | As per mfg. | EN 101 |
| 3 | Skid Resistance (Friction Coefficient) | As per mfg. | ISO-10545-17 |
| E | CHEMICAL PROPERTIES | ||
| 1 | Frost Resistance | Frost Proof | ISO-10545-12 |
| 2 | Chemical Resistance | No Damage | ISO-10545-13 |
| 3 | Stain Resistance | Resistance | ISO-10545-14 |
| F | THERMAL PROPERTIES | ||
| 1 | Thermal Shock Resistance | No Damage | ISO-10545-9 |
| 2 | Thermal Expansion | < 9 x 10-6 | ISO-10545-8 |
| 3 | Moisture Expansion | Nil | ISO-10545-10 |
GVT (glasuuritud klaasistatud plaatide) portselani mõõtmete ja pinnakvaliteedi standardid tagavad suure täpsuse ja esteetilise väärtuse. Pikkuse ja laiuse kõrvalekaldeid kontrollitakse ± 0,5%piires, samas kui paksuse variatsioonid on piiratud ± 5,0%. Kõik sirged, ristkülikukujulisus ja pinna tasasus hoitakse kõik ± 0,5%piires, tagades paigaldamise ajal täpse plaatide joondamise. Läikikust mõõdetakse läikivarveri abil sõltuvalt pinna viimistlusest ja värvierinevused peavad välimuse ühtluse säilitamiseks jääma muutumatuks.
GVT portselanist plaatidel on tugevad struktuurilised omadused. Vee imendumine on väiksem kui 0,50%, muutes need plaadid ideaalseks niiskusega kokkupuutuvate alade jaoks. Tihedusega üle 2,0 g/cm3, on need kompaktsed ja vastupidavad, tagades pikaajalise jõudluse kõrge liiklusega ja kõrge moistorite keskkonnas.
Nendel plaatidel on muljetavaldav mehaaniline tugevus, mille rebenemismoodul (paindetugevus) on vähemalt 35 n/mm², mis näitab suurt vastupidavust painutamisele ja stressile. Korraldustugevust hinnatakse vähemalt 1300 N, mis tagab, et plaadid taluvad märkimisväärset survet ilma purunemiseta. Löögikindluse määrab tootja, kinnitades veelgi plaatide vastupidavust keerulistes tingimustes.
Pinna hõõrdumiskindlust, MOHS -i kõvadust ja libisemiskindlust testitakse tootja spetsifikatsioonide põhjal, tagades, et GVT portselanist plaadid säilitavad nende pinna terviklikkuse ja vastupidavuse kulumisele aja jooksul. Need omadused on eriti olulised kõrge liiklusega piirkondades ja sagedase hõõrdumisega kokkupuutuvate pindade jaoks.
GVT portselanist plaatide keemilised omadused muudavad need väga vastupidavaks ja sobivad nii sise- kui ka välistingimustes kasutamiseks. Need on külmakindlad, muutes need ideaalseks külmemaks kliimaks. Samuti seisavad need vastu keemilistele kahjustustele, mis ei näita agressiivsete kemikaalidega kokkupuutel kulumismärke. Nende plekikindlus tagab, et pind püsib puhtana ja säilitab selle esteetilise atraktiivsuse pikema perioodi jooksul.
GVT portselanist plaadid on termilise šoki suhtes väga vastupidavad, mis tähendab, et kiirete temperatuurimuutuste tõttu ei pragune ega kahjusta. Soojuspaisumistegurit hoitakse alla 9 x 10⁻⁶ ja niiskuse laienemine on null, tagades, et plaadid säilitavad oma kuju ja terviklikkuse isegi kõikuva temperatuuri või kõrghäälikkusega keskkonnas. Need termilised omadused muudavad need sobivaks nii sise- kui ka välistingimustes.
| NO. | CHARACTERISTICS | REQUIREMENT (AS PER ISO-13006/EN14411 GROUP Bla) | ISO / EN TESTING METHOD |
|---|---|---|---|
| A | DIMENSION & SURFACE QUALITY | ||
| 1 | Deviation in length & width | ± 0.6% | ISO-10545-2 |
| 2 | Deviation in thickness | ± 0.5% | ISO-10545-2 |
| 3 | Straightness in side | ± 0.5% | ISO-10545-2 |
| 4 | Rectangularity | ± 0.6% | ISO-10545-2 |
| 5 | Surface flatness | ± 0.5% | ISO-10545-2 |
| 6 | Glossiness | - | GLOSSOMETER |
| B | STRUCTURAL PROPERTIES | ||
| 1 | Water Absorption | < 0.50% | ISO-10545-3 |
| 2 | Density (g/cc) | > 2.0 g/cc | DIN 51082 |
| C | MASSIVE MECHANICAL PROPERTIES | ||
| 1 | Flexural Strength * | > 27 N/mm ² | ISO-10545-4 |
| 2 | Breaking Strength * | 1113 N | ISO-10545-4 |
| D | SURFACE MECHANICAL PROPERTIES | ||
| 1 | Mohs hardness * | > 6 | EN 101 |
| 2 | Abrasion resistance | >175 mm ³ | ISO-10545-6 |
| 3 | Skid Resistance (Friction Coefficient) | > 0.4 | ISO-10545-17 |
| E | CHEMICAL PROPERTIES | ||
| 1 | Frost resistance | Frost proof | ISO-10545-12 |
| 2 | Chemical Resistance | No Damage | ISO-10545-13 |
| 3 | Stain Resistance | Resistant | ISO-10545-14 |
| F | THERMAL PROPERTIES | ||
| 1 | Thermal Shock Resistance | No Damage | ISO-10545-9 |
| 2 | Thermal Expansion | < 9 x 10-6 | ISO-10545-8 |
| 3 | Moisture Expansion | Nil | ISO-10545-10 |
Lahustuvate soola portselanist plaatide mõõtmete ja pinna kvaliteet tagavad täpsuse ja visuaalse atraktiivsuse. Pikkuse ja laiuse kõrvalekalded on piiratud ± 0,6%-ga, samas kui paksuse variatsiooni kontrollitakse ± 0,5%piires. Külgede ja ristkülikukujulisuse sirge hoitakse vastavalt ± 0,5% ja ± 0,6%, tagades sujuva paigaldamise. Pinna tasapinnaline kõrvalekalle on piiratud ± 0,5%-ga. Plaatide pinna läikivust mõõdetakse glossomeetri abil.
Nendel plaatidel on suurepärased struktuurilised omadused, mis muudavad need sobivaks nii elamu- kui ka ärirakendusteks. Vee imendumine on alla 0,50%, mis tagab niisketes tingimustes vastupidavuse. Tihedus on suurem kui 2,0 g/cm3, mis näitab tahket ja kompaktset struktuuri, mis suurendab plaatide pikaealisust ja üldist jõudlust.
Lahustuva soola portselanist plaatidel on oluline mehaaniline tugevus. Nende paindetugevus on suurem kui 27 N/mm², mis näitab nende võimet taluda painutamist ilma purunemata. Kordatugevust mõõdetakse kiirusel 1113 N, muutes need vastupidavaks rasketele koormustele ja rõhule.
Pinnaomadused on kriitilise tähtsusega piirkondade jaoks, mis on kokku puutunud suure liikluse ja kulumisega. Plaatide kõvadus on suurem kui 6, pakkudes tugevat vastupidavust kriimustustele ja pinnakahjustustele. Neil on kulumiskindlus suurem kui 175 mm³, mis tähendab, et nad säilitavad oma pinna kvaliteedi pikema aja jooksul. Libisetakistus (hõõrdetegur) on üle 0,4, tagades turvalisema pinna kõndimise, eriti niisketes tingimustes.
Lahustuvate soola portselanist plaatide keemilised omadused tagavad nende vastupidavuse erinevates keskkondades. Need on külmakindlad, muutes need ideaalseks külma kliima jaoks. Neil on ka kemikaalide suhtes kõrge vastupidavus, mis ei näita agressiivsete ainetega kokkupuutel kahjustusi. Nende vastupanu värvimisele tagab, et plaadid säilitavad aja jooksul oma esteetilise atraktiivsuse, isegi piirkondades, mis on kalduvad lekkeid ja mustust.
Need plaadid pakuvad suurepäraseid termilisi omadusi, muutes need sobivaks mitmekesiseks kliimaks. Need on vastupidavad termilise šoki suhtes, mis tähendab, et temperatuuri järskude muutuste tõttu ei purune nad ega kahjusta. Soojuspaisumistegur on alla 9 x 10⁻⁶ ja neil pole niiskuse laienemist, tagades mõõtmete stabiilsuse isegi kõikuva temperatuuri ja niiskuse tingimustes.
| NO. | CHARACTERISTICS | REQUIREMEN (As per 2556 (part I) 1994) |
|---|---|---|
| 1 | CRAZING TEST | No crazing up to 2 Cycle up to 5 hrs. Each Cycle up to 10 hrs. at pressure 0.34 to 0.37 Mps. |
| 2 | WATER ABSORPTION | Average Value should not exceed more than 0.5% |
| 3 | MODULUS OF REPTURE | Not less than 60 Mps. |
| 4 | CHEMICAL RESISTANCE | No less than of the glaze when compared with control sample |
| 5 | RESISTANCE TO STRAINING & BURNING | No stain shall remain on either of test piece |
| 6 | WAVY FINISH | None on all visible surface |
| 7 | DISCOLORATION | None on all visible surface |
Hoolumise test: See test hindab pinna glasuuri vastupidavust stressi all. Sanitaarhooldus ei tohiks pärast kahe surveravi tsükli läbimist mitte hullutada - see on kuni viis tundi ja kokku kümme tundi surve all vahemikus 0,34 kuni 0,37 MPa.
Vee imendumine: See spetsifikatsioon näitab materjali maksimaalset lubatud vee imendumist. Keskmine väärtus ei tohi ületada 0,5%, tagades, et toode on niiskuse suhtes vastupidav ja säilitab selle konstruktsiooni terviklikkuse.
Rebenemismoodul: See vara mõõdab sanitaartehikute tugevust. Rebenemismoodul peaks olema vähemalt 60 MPa, mis näitab, et materjal talub olulist stressi ilma purunemata.
Keemiline vastupidavus: Sanitaarvedadel peab kemikaalidele olema piisav vastupidavus. See nõue tagab, et glasuuri vastupidavus on võrreldav kontrollprooviga, kinnitades selle võimet taluda kokkupuudet erinevate ainetega ilma halvenemiseta.
Vastupanu värvimisele ja põletamisele: See iseloomulik hindab pinna võimet plekkidele ja kuumusele vastu seista. Pärast kindlaksmääratud tingimustega kokkupuudet ei tohiks ühegi katsetüki värvimine olla, mis näitab toote vastupidavust ja puhastamise lihtsust.
Laineline viimistlus: Sanitaartoodete viimistlus peaks olema sujuv, ilma nähtavate pindade lainelisuseta. See kriteerium tagab esteetilise veetluse ja praktilise kasutatavuse.
Muutus: Sanitaartehnid ei tohiks näidata nähtavatel pindadel värvimuutust. See nõue tagab, et toode säilitab aja jooksul kavandatud välimuse, suurendades klientide rahulolu ja toote pikaealisust.
| NO. | CHARACTERISTICS | STANDARD TEST | RESULT |
|---|---|---|---|
| 1 | APP. DENSITY KG/DM3 | EN14617-1 | 2.2-2.45 |
| 2 | WATER ABSORPTION | EN14617-1 | < 0.04 |
| 3 | FLEXURAL TRENGTH (MPA) | EN14617-2 | 50-60 |
| 4 | DIMENSIONAL STABILITY | EN14617-12 | CLASS A |
| 5 | IMPACT RESISTANCE (JOULE) | EN14617-9 | 4-9 JOULE |
| 6 | COMPRESSIVE STRENGTH (MPA) | EN14617-15 | 170-220 |
| 7 | ABRASION RESISTANCE | EN14617-4 | GROOVE LENGTH=21.1 MM |
| 8 | FROST RESISTANCE | DIN 52104 | COMPLIES WITH STANDARD |
| 9 | SURFACE HARDNESS (HOHS SCALE) | EN 101 | 6.0-7.0 |
| 10 | STAIN RESISTANCE | ANSI Z124.6 | PASS |
| 11 | WEAR & CLEANABILITY | ANSI Z124.6 | PASS |
| 12 | CHEMICAL RESISTANCE | ANSI Z124.6 | PASS |
| 13 | CHEMICAL RESISTANCE | EN14617-10 | CLASS C4 |
| 14 | RESISTANCE TO ACIDS | ASTM C 650 | NOT AFFECTED |
| 15 | LINEAR THERMAL EXPANSION (300-600) 0C-1 | EN14617-11 | 2.6x10-6 |
| 16 | BOILING WATER RESISTANCE | NEMA LD3-3.5 | PASS |
| 17 | HIGH TEMPERATURE RESISTANCE | NEMA LD3-3.6 | PASS |
| 18 | CIGARETTE TEST | ANSI Z124.6 | PASS |
| 19 | FIRE CLASSIFICATION | EN13501-1 | WALL CLADDING: B-S1-D0,FLOORING & STAIR: B-F1-S1 |
| 20 | SLIP RESISTANCE | EN 14231 | WET: 13-21 SRV, DRY: 43-53 SRV |
| 21 | REDIATION | GB 6566-2010 | COMPLIES WITH REQUIREMENT OF STANDARD |
| 22 | THERMAL SHOCK RESISTANCE | EN14617-6 | NO VISUAL DEFECTS AFTER 10 CYCLE |
| LOSS IN FLEXURAL STRENGTH = LOSS IN MASS = 0.02%-0.05% 0.07%-1.1% | |||
| 23 | FREEZE & THAW RESISTANCE | EN14617-5 | NO DEFECTS AFTER 25 FREEZE-THAW CYCLE |
| 24 | GLOSSINESS REFLECTION | % | 45-70 |
| 25 | SURFACE SLIP RESISTANCE HONED 400 | DIN 51130 | R9 |
| 26 | STATIC COEFFICIENT OF FRICTION | ASTM C 1028 | DRY: 0.8, WET: 0.6 |
Quartz Stone tehnilised spetsifikatsioonid hõlmavad erinevaid kriitilisi omadusi, mis tagavad selle kvaliteedi, vastupidavuse ja sobivuse erinevatele rakendustele. Näiline tihedus on vahemikus 2,2 kuni 2,45 kg/dm³, mis näitab selle tugevat füüsilist struktuuri. Lisaks on vee imendumine minimaalne, mõõdetuna alla 0,04%, tagades, et kivi on niiskuse suhtes läbitungimatu. Paindetugevus jääb vahemikku 50–60 MPa, kajastades selle võimet taluda paindejõude, samal ajal kui survetugevus ulatub vahemikku 170–220 MPa, rõhutades selle tugevust vertikaalsete koormuste korral.
Muud olulised testid hõlmavad hõõrdumiskindlust, soone pikkus on 21,1 mm, ja külmakindlus, mis vastab tööstusstandarditele. Quartz Stone näitab ka suurepärast plekki, kulumist ja keemilist vastupidavust, mille tulemused ei näita kahjulikke mõjusid. Veelgi enam, see läbib erinevaid soojuskindlustustestid, sealhulgas keeva veekindlus ja kõrge temperatuuriga vastupidavus. Üldiselt kinnitavad need spetsifikatsioonid, et kvartskivi on mitmekülgne, vastupidav materjal, mis sobib nii esteetiliseks kui ka funktsionaalseks rakenduseks ehitamiseks ja disainiks.